【摘 要】
：
To investigate the evolution of microstructure and wear behavior of TiSiN coatings with the variation of Si in targets and lays the foundation for its controllable mass production,Ti(1-x)SixN composite coatings were deposited onto Si (100) and cemented ca
【机 构】
：
School of Engineering, Huazhong Agricultural University, Wuhan 430070, China;School of Power & Mecha
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
To investigate the evolution of microstructure and wear behavior of TiSiN coatings with the variation of Si in targets and lays the foundation for its controllable mass production,Ti(1-x)SixN composite coatings were deposited onto Si (100) and cemented carbide substrates using TiSi targets with different Si content by cathodic arc ion plating.The influences of Si on the microstructure and mechanical properties were studied.Nano-amorphous composite structure appeared in the Ti(1-x)SixN coatings when Si content in TiSi target was higher than 5at％.However,further increase of Si content in TiSi target exhibited a negligible effect on the microstructure of Ti(1-x)SixN coatings.Hardness and deformation resistance were correlated to the content of Si in TiSi targets.Maximum hardness was obtained as the Si content in target increased up to 20at％.Friction coefficient and wear rate significantly decreased with addition of Si in TiN coating,and then dually increased with the increase of Si content in targets.
其他文献
Herein, two nanoparticles with different dimensions, spherical carbon dots (C-dots) and sheet-like hectorite clay, were used as physical crosslinkers to fabricate C-dots-clay-poly(N-isopropylacrylamide) nanocomposite hydrogels (coded as C-dots-clay-PNIPAm
To evaluate the property and degradation characteristics of concrete prepared with aggregate contained montmorillonite,concretes were prepared with aggregates contained montmorillonite,and then concrete slump loss,compressive strength,electric flux,the re
2198 and 5A90 Al-Li alloys were anodized with a constant DC potential in 18％H2SO4 solution (Solu.A) and the mixture solution of 18％H2SO4+5％C2H2O4 (Solu.B) at room temperature.12 and 11 V was optimized as the applied oxidation potential for 2198 and 5A90 a
A niobate/titanat nanoflakes (Nb/TiNFs) composite was synthesized via the hydrothermal method and used to remove Pb(II) from water. XRD, TEM, and SEM results indicate that Nb/TiNFs appear as nanoflakes, of which the primary crystal phase is tri-titanate.
The modification of graphitic carbon nitride can significantly improve the photocatalytic performance of graphitic carbon nitride (g-C3N4). Fe2O3/nitrogen-deficient g-C3N4-x composite catalysts were prepared with dicyandiamide as the precursor and Fe3+ do
Based on the experimental analysis and theoretical calculation,the self-propagating high temperature synthesis of TiB2/Fe composite was studied.The experimental results show that the interfacial between TiB2 and Fe was smooth and clear,and the composite b
SiC/7075 aluminum matrix composites were prepared by a liquid stirring method. The role of Ti facilitating the preparation of SiC/7075 aluminum matrix were studied by means of direct-reading spectrometer, scanning electron microscope, energy dispersive sp
The aluminum matrix composites (AlB2+α-Al2O3)/Al were fabricated by in situ reaction synthesis from an Al-B2O3 system. The reaction pathways, apparent activation energies and tensile properties were analyzed by using differential scanning calorimetry (DSC
Three as-cast and as-extruded Mg-5Zn-xY-0.6Zr (x=5 wt％,8 wt％,11 wt％) alloys were prepared,and the effects of Y content on the microstructures and mechanical properties of the alloys were investigated.The results show that the investigated Mg-Zn-Y-Zr alloy
We presented a simple yet convenient hydrothermal approach for the large-scale synthesis of uniform cylindrical silver (Ag) single-crystalline nanowires with diameters of about 25 nm and lengths of 1-4 μm. Poly(vinyl pyrrolidone) (PVP) was used as a reduc