【摘 要】
：
研究了镁合金轮椅小轮轴套焊接部位的结构,改变了焊道的部位和方向,大大降低了焊接部位应力集中,有效地提高了焊接部位的疲劳强度。结果表明:焊道长度与疲劳性能有一定的关系
【机 构】
：
浙江工贸职业技术学院先进材料研发中心,
论文部分内容阅读
研究了镁合金轮椅小轮轴套焊接部位的结构,改变了焊道的部位和方向,大大降低了焊接部位应力集中,有效地提高了焊接部位的疲劳强度。结果表明:焊道长度与疲劳性能有一定的关系,当焊道长度大于25 mm时,其疲劳寿命可达21万次以上,根据GB/T13800-2009标准测试满足轮椅的使用要求。
The structure of the welded parts of magnesium alloy wheelchair wheel hub was studied, the location and orientation of the weld bead were changed, the stress concentration in the welded part was greatly reduced, and the fatigue strength of the welded part was effectively improved. The results show that there is a certain relationship between the weld bead length and the fatigue performance. When the weld bead length is greater than 25 mm, the fatigue life of the weld bead reaches more than 210,000 times. According to the GB / T13800-2009 standard test, the wheelchair requirements are met.
其他文献
目的 通过手术对照,探讨急诊三维CT血管造影(3D-CTA)在前循环动脉瘤的临床应用及其价值,同时为了检验3D-CTA检查的诊断符合情况.方法 59例自发性蛛网膜下腔出血(SAH)患者,其
目的 观察骨髓间充质干细胞(BMSC)移植治疗杜氏型肌营养不良(DMD)治疗前后血清酶学变化及临床效果.方法 选择2007年6月至2009年6月解放军第四六三医院515例DMD患者,其中男性5
目的 测定高压氧治疗患者头罩内的氧气体积分数.方法 10例高压氧治疗患者,其中男性7例,女性3例;年龄22～72岁,平均年龄52.2岁.全部气管切开.将氧气流速设定为8、10、15I/min,治
抽动秽语综合征(TS)是神经精神疾病,病程反复,近几年发病率升高,临床缺乏客观指标评价TS及估计预后,最近解剖学和神经影像学研究提示,TS患者较正常人基底节区及额叶、边缘系
目的 利用光学相干断层扫描(OCT)测量并分析早期糖尿病(DM)患者的黄斑区视网膜厚度.方法 正常对照组30例60只眼,其中男性15例,女性15例;年龄38～71岁,平均年龄51岁.DM组60例120
糖尿病足是糖尿病的主要慢性并发症之一.足部外伤合并感染导致溃疡、坏疽,甚至使患者面临截肢的危险,严重地影响糖尿病患者的生活质量.干细胞治疗能有效促进新血管生成、促进
目的 表达及纯化8羟基脱氧鸟苷DNA糖苷酶-1(OGG1)融合蛋白制备多克隆抗体.方法 在大肠杆菌BL21中诱导表达OGG1融合蛋白,应用Ni-NTA亲和树脂进行纯化.纯化后的OGG1融合蛋白多
目的 观察局部注射重组人干扰素α-2b注射液联合口服泛昔洛韦治疗频发性生殖器疱疹的临床疗效及复发率.方法 86例频发性生殖器疱疹患者,其中男性63例,女性23例;年龄19～54岁,平
目的探讨不同疗程的重组人干扰素(IFN)α-2b(安福隆)治疗乙型肝炎病毒e抗原(HBeAg)阳性慢性乙型肝炎(CHB)的疗效并比较随访12个月的结果。方法 72例CHB患者,其中男性46例,女
目的 探讨XRCC1 Codon399单核苷酸多态性与鼻咽癌患者正常组织急性放射反应的相关性.方法 收集经病理学检查确诊的鼻咽低分化鳞癌患者60例,于放疗前抽取静脉血,抽取全血基因