By means of electron backscattering diffraction and transmission electron microscopy the microstructure and texture of drawn single crystal copper with initial orientation <110> parallel to axial direction have been investigated in the present work.In or-der to analyze the effect of initial orientation on microstructure and texture of drawn copper,the results of the drawn <110> sin-gle crystal copper wires have been compared with <100> and <111> single crystal copper wires.It is found that the grain subdi-vision of <110> single crystal is more evident than that of <100> and <111>,and the textures consisting of <111> and <100> abruptly form in the drawn <110> single crystal.At high strains,due to shear strain,the distribution of fiber textures is imho-mogenous along the radial direction of drawn <110> single crystal copper wires.<100> is near the surface and <111> is at the center.The microstructure results of drawn <110> single crystal show that at low strains,it can be characterized as two kinds of geometrically necessary boundaries with noncrystalline character.At medium strains,S bands can be observed.At high strains,lamellar boundaries form.Mean misorientation and average spacing of dislocation boundary are larger in drawn <110> single crystal,as compared with <111> and <100>.In drawn <110> single crystal with high strains,the bimodal distribution forms at lower strains than in drawn <100> single crystal,which is because the dislocation boundaries with high angle are contributed by not only the boundary between <111> and <100> fiber textures but also the boundary in <111> or <100> texture.
By means of electron backscattering diffraction and transmission electron microscopy the microstructure and texture of drawn single crystal copper with initial orientation <110> parallel to axial direction have been investigated in the present work. In or-der to analyze the effect of initial orientation on microstructure and texture of drawn copper, the results of the drawn <110> sin-gle crystal copper wires have been compared with <100> and <111> single crystal copper wires.It is found that the grain subdivision-of <110> single crystal is more evident than that of <100> and <111>, and the textures consisting of <111> and <100> abruptly form in the drawn <110> single crystal. At high, due to shear strain, the distribution of <100> is near the surface and <111> is at the center. microstructure results of <110> single crystal show that at low It can be characterized a s two kinds of geometrically necessary boundaries with noncrystalline character. At medium strains, S bands can be observed. At high strains, lamellar boundaries form. Muni misorientation and average spacing of dislocation boundaries are larger in <110> single crystal, as compared with <111> and <100>. In drawn <110> single crystal with high, the bimodal distribution forms at lower than than drawn in <100> single crystal, which is because the dislocation boundaries with high angle are contributed by not only the the boundary between <111> and <100> fiber textures but also the boundary in <111> or <100> texture.