【摘 要】
：
Precipitation behavior of (Ti,V,Mo)C and microstructural evolution of the ferritic Ti-V-Mo complex microalloyed steel were investigated through changing coiling temperature (CT). It is demonstrated that the strength of the Ti-V-Mo microalloyed steel can b
【机 构】
：
Key Laboratory of Metallurgical Emission Reduction and Resources Recycling, Anhui University of Tech
论文部分内容阅读
Precipitation behavior of (Ti,V,Mo)C and microstructural evolution of the ferritic Ti-V-Mo complex microalloyed steel were investigated through changing coiling temperature (CT). It is demonstrated that the strength of the Ti-V-Mo microalloyed steel can be ascribed to the combination of grain refinement hardening and precipitation hardening. The variation of hardness (from 318 to 415 HV, then to 327 HV) with CT (from 500 to 600-625℃,then to 700℃) was attributed to the changes of volume fraction and particle size of (Ti,V, Mo)C precipitates. The optimum CT was considered as 600-625 ℃, at which the maximum hardness value (415 HV) can be obtained. It was found that the atomic ratios of Ti, V and Mo in (Ti, V, Mo)C carbides were changed as the CT increased. The precipitates with the size of ＜ 10 nm were the V-rich particles at higher CT of 600 and 650 ℃, while the Ti-rich particles were observed at lower CT of 500 and 550 ℃. Theoretical calculations indicated that the maximum nucleation rate of (Ti, V, Mo)C in ferrite matrix occurred around 630 ℃, which was consistent with the 625 ℃ obtained from experiment results.
其他文献
The relationship between the tensile properties and δ (delta) phase precipitation in cast alloy IN625 was investigated in this paper.Although the influences of δ phase on the mechanical properties have been pointed out in our previous work,the relationshi
Based on equiatomic nickel and titanium,three kinds of NiTiFe alloys with a nominal chemical composition of Ni49Ti49Fe2,Ni48Ti48Fe4 and Ni47Ti47Fe6 (at.％),respectively,have been designed to investigate the influence of the addition of Fe element on phase
Copper matrix composites were prepared through spark plasma sintering (SPS) process,mixing fixed amount of reduced graphene oxide (rGO) with the different amounts of Cr.In the sintered bulk composites,the layered rGO network and uniform Cr particles distr
As-cast microstructure of a designed polycrystalline Ni3Al-based superalloy is characterized using optical microscope,scanning electron microscope,transmission electron microscope equipped with selected area diffraction system,and the intermetallic phase
The influence of Nb content on the microstructure and cryogenic mechanical properties of a 7％Ni steel was investigated within the Nb content range from 0 to 0.05％. The microstructure was characterized by optical microscope, scanning electron microscope, t
The effect of open porosity of Y2O3 ceramic on the apparent contact angle and interaction between molten Ti47Al alloy and Y2O3 ceramic substrates under pure Ar was investigated by using a sessile drop method at 1600 ℃.As the open porosity increased from 9
Carbon dioxide mineral sequestration with steelmaking slag is a promising method for reducing carbon dioxide in a large-scale setting.Existing calcium oxide or calcium hydroxide in steelmaking slag can be easily leached by water,and the formed calcium car
Wear behaviors of 3Cr2W8V and GH4169 with H70, including surface property, wear performance and friction work, were investigated. 3Cr2W8V and H70 friction pair suffered severer wear and surface damage than GH4169 and H70 friction pair. The wear process ha
The synthetic effects of frequency and duty ratio on growth characteristics and corrosion properties of coating on Ti6Al4V fabricated by microarc oxidation are investigated comprehensively.Under the condition of uniform cumulating time of positive impulse