The as-rolled AZ31 Mg alloy sheets are welded by friction stir welding (FSW) in this study,followed by annealing and hot rolling with different reductions.The effects of welding speed and the rolling reduction on the microstructure,tensile properties,micr
【机 构】
：
College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China;National
论文部分内容阅读
The as-rolled AZ31 Mg alloy sheets are welded by friction stir welding (FSW) in this study,followed by annealing and hot rolling with different reductions.The effects of welding speed and the rolling reduction on the microstructure,tensile properties,microhardness and fracture surfaces of the specimens are investigated.The results show that the microstructures of the FSW joint in different regions become more and more consistent as the hot rolling reduction increases.The mechanical properties of the FSW joints and the joint coefficient are improved with increasing rolling reduction;however,the hardness value in the stirred zone decreases firstly and then increases.When the rolling reduction is 50％,the tensile strength of FSW joint is close to that of base metal.The sample L3 achieves the best comprehensive properties,with the yield strength,ultimate tensile strength and elongation of 162,287.9 MPa,and 17.9％,respectively.
其他文献
The σ-phase precipitation in 20％ cold-worked 15Cr-15Ni titanium-modified austenitic stainless steel was studied during long-term aging treatment.During the isothermal aging stage,the amount of σ-phase was significantly increased at beginning and gradually
It has been widely demonstrated that addition of Ni in low-carbon steels can effectively improve the cryogenic toughness,but the mechanism behind it has yet to be clarified.In the present work,the evolutions of microstructure and mechanical properties aft
2.98 kGy/h (1007 h) gamma irradiation and 90 ℃ (2000 h) thermal aging were exerted to X65 grade low carbon steel buried in Gaomiaozi bentonite containing 17 wt％ Beishan groundwater.The average corrosion rate of X65 low carbon steel was measured.The elemen
The effect of electropulsing on the mechanical behaviors and microstructures of Ti-6Al-4V titanium alloy was investigated by an uniaxial tensile test.Compared to the value measured in cold tensile test,the alloy exhibits lower ultimate tensile strength wh
Despite the economy of material cost and excellent toughness of Cu-based amorphous alloys,especially Cu5oZr5o,their poor corrosion resistance to a chloride medium limits their widespread applications.In this study,corrosion tests were performed on the Cu5
The hot deformation characteristics and the corrosion behavior of a high-strength low-alloy (HSLA) steel were investigated at deformation temperatures ranging from 800 to 1100 ℃ and strain rates ranging from 0.1 to 10 s-1 using an MMS-200 thermal simulati
The tensile tests of AZ31 magnesium alloy were carried out under room temperature,100,150 and 200 ℃ with and without pulse current.The effect of temperature on dynamic recrystallization (DRX) of AZ31 alloy was studied at different conditions.One-parameter
The voltage was recorded to investigate the influence of the static magnetic field on droplet evolution during the magnetically controlled electroslag remelting (MC-ESR) process.MC-ESR experiments were carried out under different remelting current,and tra
In this study,the degradation efficiencies of zero-valent iron (ZVI) powders with different structures and components were evaluated for methyl orange (MO).The results show that the structure is an essential factor that affects degradation,and added non-m
The tribocorrosion behavior of 304 stainless steel was studied through comparing the damage behavior of 304 stainless steel in dilute sulfuric acid to that in distilled water by a reciprocating tribotester.The re-passivation behavior,the surface and secti