The FeNip/PP nanocomposites were successfully prepared by the two-step blending method and the permeable layer interface with thickness of 2 to 10 nm was formed on the surface of nanopowders. The interface is composed of the lattice and molecular chain, i
【机 构】
：
College of Material Science and Engineering, Nanchang University, Nanchang 330031, China
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The FeNip/PP nanocomposites were successfully prepared by the two-step blending method and the permeable layer interface with thickness of 2 to 10 nm was formed on the surface of nanopowders. The interface is composed of the lattice and molecular chain, in which the polypropylene molecular chain enters the lattice defects and forms a cross-linked structure. The interface causes the FeNi nanopowders to be well compatible with the polypropylene matrix and uniformly dispersed in the matrix, and significantly improves the mechanical properties of composites. The tensile strength of 2wt％ FeNip/PP composites reached 38 MPa, 23％higher than that of pure PP resin. The shielding performance of 20wt％ FeNip/PP composites reached 9.8 dB in the frequency range of 1-100 MHz.
其他文献
Using lignite-based hypercoal as raw material, KOH as activator and CuO as microwave absorber, we prepared hypercoal-based activated carbons by microwave-assisted activation. The pore structure and the electrochemical performance of the activated carbons
The amorphous I/Au composite nanofilms were prepared by low vacuum direct current sputtering (LVDCS) method. The optimized preparation technologies contain growth pressure, time, gaseous environment and annealing conditions. The maximum fluorescence emiss
Chitosan (CS), hydrated zinc acetate, and rectorite (REC) were used as raw materials to prepare CS-embedded zinc oxide (ZnO) nanoparticle by a chemical precipitation process. Hydrogen-bonded REC-loaded ZnO-CS nanoparticle was to form ZnO-CS/REC nanocompos
Ionic liquid modified silica nanoparticles were synthesized using a simple silane chemistry,followed by substitution reaction.The phenol adsorption performance was tested using temperature programmed desorption technique.The experimental results reveal th
Mechanical systems on all length scales may be subjected to nanoscale thin film lubrication (TFL). Molecular dynamics (MD) simulations were conducted to investigate the lubrication mechanism and boundary slip of squalane confined in nanogap at 293 K with
The influences of new, scrap, and five modified Mo fibers on interface bonding strength of fiber-matrix and mechanical strength of RMC were studied. Typical specimens with different fibers and mass ratio of resin and hardener were prepared to verify the a
Mg-6Zn-xCe (x =0,0.6,1.0,2.0) alloy ingots with diameter of 50 mm were extruded into bars with diameter of 12 mm at 300 ℃.The microstructures were analyzed by X-ray diffraction,optical microscopy,scanning electron microscopy and transmission electron micr
A self-regulating humidity material with bamboo for the room was prepared. The activated carbons were prepared with the temperature rising rates of 5, 10, 15, 20 ℃/min and constant temperatures of 600, 700, 800, 900, 1000, 1100, 1200, 1300, 1400, and 1500
PEO ceramic coatings including ZrO2-Al2O3-SiO2 in three phases were prepared on an Al-12.5％Si alloy in electrolyte solutions containing ZrO2 nanoparticles.The microstructures and phases of the coatings were analyzed by SEM and XRD,and the heat insulation
A novel method was presented to create composite micelles of amphiphilic copolymers and Ag nanoparticles (NPs) in a three-dimensional co-flow focusing microfluidic device (3D CFMD). Self-assembly of the copolymers was initiated by the fast mixing of water