【摘 要】
：
PEO ceramic coatings including ZrO2-Al2O3-SiO2 in three phases were prepared on an Al-12.5％Si alloy in electrolyte solutions containing ZrO2 nanoparticles.The microstructures and phases of the coatings were analyzed by SEM and XRD,and the heat insulation
【机 构】
：
Shaanxi Key Laboratory of Photoelectric Functional Materials and Devices, School of Materials and Ch
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
PEO ceramic coatings including ZrO2-Al2O3-SiO2 in three phases were prepared on an Al-12.5％Si alloy in electrolyte solutions containing ZrO2 nanoparticles.The microstructures and phases of the coatings were analyzed by SEM and XRD,and the heat insulation performance and the thermal shock resistance of the coatings were investigated.The compactness of the coating increased significantly and the hindrance of the Si element on plasma electrolytic oxidation process was effectively weakened.The growth rate of the coating was improved substantially with the addition of ZrO2 nanoparticles.The PEO ceramic coatings are primarily composed of SiO2 and high temperature steady phases such as α-Al2O3 and c-ZrO2.Both the content of c-ZrO2 and the heat-insulating property of the coating increased significantly.The ceramic coatings with special microstructure and composition formed in the solutions containing ZrO2 nanoparticles possess excellent heat insulation performance and thermal shock resistance.
其他文献
A combination of experimental measurements and numerical analysis was utilized to study the low-velocity impact damage of domestic carbon fiber-reinforced composites (CFRCs). The results indicated that the low-velocity impact damage induced pits and longi
A Fe modified Na2WO4 compound was synthesized by a solution impregnation method and was ball-milled with MgH2 to constitute a novel MgH2-Fe2O3/Na2WO4 composite. The effects of the Fe2O3/Na2WO4 additive on the hydrogen storage properties of MgH2 together w
Using lignite-based hypercoal as raw material, KOH as activator and CuO as microwave absorber, we prepared hypercoal-based activated carbons by microwave-assisted activation. The pore structure and the electrochemical performance of the activated carbons
The amorphous I/Au composite nanofilms were prepared by low vacuum direct current sputtering (LVDCS) method. The optimized preparation technologies contain growth pressure, time, gaseous environment and annealing conditions. The maximum fluorescence emiss
Chitosan (CS), hydrated zinc acetate, and rectorite (REC) were used as raw materials to prepare CS-embedded zinc oxide (ZnO) nanoparticle by a chemical precipitation process. Hydrogen-bonded REC-loaded ZnO-CS nanoparticle was to form ZnO-CS/REC nanocompos
Ionic liquid modified silica nanoparticles were synthesized using a simple silane chemistry,followed by substitution reaction.The phenol adsorption performance was tested using temperature programmed desorption technique.The experimental results reveal th
Mechanical systems on all length scales may be subjected to nanoscale thin film lubrication (TFL). Molecular dynamics (MD) simulations were conducted to investigate the lubrication mechanism and boundary slip of squalane confined in nanogap at 293 K with
The influences of new, scrap, and five modified Mo fibers on interface bonding strength of fiber-matrix and mechanical strength of RMC were studied. Typical specimens with different fibers and mass ratio of resin and hardener were prepared to verify the a
Mg-6Zn-xCe (x =0,0.6,1.0,2.0) alloy ingots with diameter of 50 mm were extruded into bars with diameter of 12 mm at 300 ℃.The microstructures were analyzed by X-ray diffraction,optical microscopy,scanning electron microscopy and transmission electron micr
A self-regulating humidity material with bamboo for the room was prepared. The activated carbons were prepared with the temperature rising rates of 5, 10, 15, 20 ℃/min and constant temperatures of 600, 700, 800, 900, 1000, 1100, 1200, 1300, 1400, and 1500