Different failure modes and morphologies were found in the chemical vapor infiltration (CVI) 2D C/SiC torque tubes with different thickness. To characterize the density and porosity of the ceramic matrix composite (CMC) torque tube, a CT test was conducte
【机 构】
：
Science and Technology on Thermostructure Composite Materials Laboratory, Northwestern Polytechnical
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Different failure modes and morphologies were found in the chemical vapor infiltration (CVI) 2D C/SiC torque tubes with different thickness. To characterize the density and porosity of the ceramic matrix composite (CMC) torque tube, a CT test was conducted. The archimedes drainage method was used to measure the density and porosity, and by adopting FEM software, the stress distribution and failure strength of the ceramic matrix composite torque tubes were calculated. A universal material test machine was used to implement torsional tests. Different torsional behaviors of CMC torque tubes with two different thicknesses were showed in the stress-strain curves. To analyze the predominant failure factors, SEM was used to observe the failure morphologies and cracks. 5 mm thickness CMC torque tube has reasonable fracture morphologies and a higher maximum shear strength and modulus.
其他文献
To improve corrosion and wear resistances of the Zirconium(Zr) based alloys which are widely applied in nuclear reactors and chemical corrosion-resistant equipment,a new surface modification scheme was designed to deposit a Zr75Cu25 coating on Zr substrat
A novel type of microencapsulated phase change materials (microPCMs) based on 1-tetradecanol (TD) core and silver-coated poly (melamine-urea-formaldehyde) (MUF) shell was successfully synthesized by in situ polymerization method followed by silver reducti
An optimal structure design of the lattice mismatched GaInP/GaInAs/Ge solar cell with high photoelectric conversion efficiency was proposed.Two-dimensional Bi2Te3 and Sb2Te3 nanosheets were prepared by solvothermal synthesis method used as thermoelectric
(ZrMg)xY2-2xMo3O12 (x=0.0, 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, and 1) ceramics have been synthesized to obtain less hygroscopicity and negative thermal expansion. With increasing the substitution of (ZrMg)6+ (ion radius 7.2 ×10-11 m) for Y3+ (ion
Polyaniline (PANI)/Ce(NO3)3 composite with short fiber-like shape was synthesized successfully in a poly (2-arcylamido-2-methylpropane sulfonic acid) aqueous solution.A comparison of SEM images found that short fiber-like composites can be obtained by con
A novel solid-gas reaction preparation technology was used to adjust the composition and microstructure of the composite crystal materials by changing the preparation parameters. Compared with the commonly used sol-gel method, acid base neutralization sed
The formation and growth behavior of intermetallic compound (IMC) layers after introducing an electroless Ni-W-P metallization into the Sn-3.0Ag-0.5Cu (SAC305) solder joint during soldering and aging were investigated.The soldering was performed at 250 ℃
The Z-type ferrites of nominal composition Ba3Co2Fe24O41+x wt％ Bi2O3, where x=0.25, 0.5, 1.0, 1.5, 2.0, were prepared by conventional ceramic processes. The influence of Bi2O3 content on the bulk densities, microstructures, magnetic and dielectric propert
A novel fiber optic sensor based on optical composite oxygen-sensitive film was developed for determination of 2,4-dichlorophenol (DCP). The optical composite oxygen-sensitive film consists of tris(2,2\'-bipyridyl) dichloro ruthenium(II) hexahydrate (Ru
The microstructure and texture evolution of Fe-33Mn-3Si-3Ai twinning induced plasticity (TWIP) steel were studied by the scanning electron microscope (SEM) and X-ray diffraction (XRD) at room temperature.After quasi-static tensile,the texture evolution of