The CdS/ spherical g-C3N4 n-n heterojunction photocatalyst was fabricated via a solvothermal method. The tetracycline was used to characterize the photocatalytic properties of the as-developed hybrids. The photocatalytic degradation mechanism of the as-de
【机 构】
：
School of Materials Science and Engineering, Hebei Provincial Key Laboratory of Traffic Engineering
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The CdS/ spherical g-C3N4 n-n heterojunction photocatalyst was fabricated via a solvothermal method. The tetracycline was used to characterize the photocatalytic properties of the as-developed hybrids. The photocatalytic degradation mechanism of the as-developed heterojunction photocatalyst was also analyzed. Research results show that CdS nanoparticles are well dispersed in the surface layer of spherical g-C3N4. Moreover, the mass ratio of CdS to spherical g-C3N4 will influence the photocatalytic activity of the as-developed composites, which shows the trend of first increasing and then decreasing as it increased. When the mass ratio is 7:1, in 25 min, the as-developed heterojunction shows 93.2 % of the maximum photocatalytic efficiency and still exhibits 83.6 % after 5 times cycle testing. Moreover, the as-developed hybrids can accelerate the electron transport and improve the separation efficiency of photo-generated carriers compared with pure samples. In addition, the holes and superoxide radicals are dominating active species during the photocatalytic degradation process.
其他文献
Nano-ZrO2 and PEEK particles were synergistically filled in unfilled PTFE to improve the wear resistance and maintain a relatively low friction coefficient, and the materials were studied using a reciprocating sliding friction and wear tester. In the fric
A post-treatment of hydrothermal process was conducted to evaluate its effects on the material characteristics and mechanical properties of plasma-sprayed pure HA and HA/20％ YSZ coatings. Surface morphology and microstructural changes, relative element co
The polymeric admixture,the sodium-carboxymethylcellulose (CMC)/poly sodium p-styrene sulfonate (PSS) / poly vinyl acetate (PVAc) was synthesized and applied in cement mortars.The polymer was tested by FTIR and SEM,and the results indicate that the ideal
The nucleation process of graphene films prepared by pulsed laser deposition has been investigated in detail. It is found that graphene nucleates at the steps on the substrate surface firstly, from aggregation of nuclei into particles. High pulsed laser e
In order to explore the effect of high-temperature annealing on the mechanical performances and microstructures of different oxygen SiC fibers, two types of silicon carbide (SiC) -based fibers, specified as XD-SiC fibers (low oxygen) and Nicalon-201 fiber
A recrystallization and partial melting (RAP) process was introduced to prepare the semi-solid 7075 aluminum alloy used for thixoforming. In order to obtain an ideal semi-solid microstructure, a series of extrusion experiments were conducted to comparativ
A plasma cladding experiment was carried out to investigate the characteristics(surface hardness, microstructure, friction, wear properties from different substrates to the cladding layer and the bond strength) of plasma cladding Fe-Cr-Nb-Si-Mo alloy clad
The 0.6mol％ CuO-doping 0.996(0.95Na0.5K0.5NbO3-0.05LiSbO3)-0.004FeBiO3 (KNN-LSBF-CuO) piezoelectric ceramics were synthesized by a solid-state reaction technique, and the structure and piezoelectric properties dependence of sintering time in KNN-LS-BF-CuO
Low-cost porous calcined dolomite microspheres were prepared by simple spray drying and subsequent calcination. Effects of calcination temperature on phase evolution and adsorption properties of MB were investigated systematically. Results showed that mic
Polystyrene crosslinked microspheres were prepared by soap-free emulsion polymerization using styrene (St) and divinylbenzene (DVB) as monomers; then, the microporous structure was knitted by the Friedel-Crafts alkylation reaction, and the Au nanoparticle