【摘 要】
：
为了使热轧板在技术上实现"以热代冷",需要进行退火以获得综合性能优异的板材.因此本文研究不同退火温度和保温时间对纯钛TA2热轧板材的显微组织和力学性能的影响.其中退火温度范围为550～700℃,保温时间分别为5min和30min.结果表明,在退火温度550℃保温5min时,发生部分回复再结晶.随保温时间的延长和退火温度的升高,晶粒不断长大.综合显微组织和性能,选择退火工艺为550℃/30min满足
【机 构】
：
北京科技大学冶金工程研究院,北京100083
论文部分内容阅读
为了使热轧板在技术上实现"以热代冷",需要进行退火以获得综合性能优异的板材.因此本文研究不同退火温度和保温时间对纯钛TA2热轧板材的显微组织和力学性能的影响.其中退火温度范围为550～700℃,保温时间分别为5min和30min.结果表明,在退火温度550℃保温5min时,发生部分回复再结晶.随保温时间的延长和退火温度的升高,晶粒不断长大.综合显微组织和性能,选择退火工艺为550℃/30min满足热轧板的退火要求.其强塑积最佳,综合性能优于冷轧板,可以代替冷轧板使用,从而实现"以热代冷".
其他文献
Cigarette smoke is an aerosol stream containing an extremely complex mixture of chemicals.Amongst the more than 5000 identified constituents of smoke, approximately 150 of these have been documented a
Shape memory polymers (SMPs) are a class of smart materials which can change their shape by external stimulus, such as temperature, humidity, light, electricity, and so on.
Cell adhesion and proliferation on poly(lactic acid) (PLA) microspheres is limited due to the lacking of hydrophilicity and surface cell recognition sites of PLA materials.
Self-healing materials, which possess the ability to repair themselves after damage, are emerging of a hot topic in polymer and material chemistry.
Cigarette smoke is a complex mixture consisting of more than five thousand chemicals, amongst which approximately 150 constituents have been documented as toxicants.
PLLA grafted from microcrystalline cellulose proved to improve the thermoplastic properties of cellulose.The cellulose-g-PLLA with different content of cellulose can be synthesized by employing ring-o
Aerogels are highly porous materials in which the typical structure of the pores and the network is largely maintained when the liquid solvent of a wet gel is replaced by air[1,2].In 1931, Kistler fir
研究了三种不同热处理制度对Ti-811合金连轧棒材显微组织及力学性能的影响,热处理制度分别为910℃/1h AC+580℃/8h AC,1010℃/1h AC+580℃/8h AC和1010℃/1h WQ+580℃/8h AC.结果表明:在时效温度不变的情况下,对比910℃/1h AC和1010℃/1h AC两种固溶制度可知,随着固溶温度的提高,初生α相减少、次生α相增多呈片层状分布,并且有晶界α
基于βTi-Mo合金以{332}孪生方式变形时屈服强度低和均匀延伸率高,而析出脆性ω相以位错滑移变形时屈服强度高和均匀延伸率低的塑性变形行为,提出预变形孪晶与ω相相结合的强韧化途径.采用金相显微镜观察、X射线衍射分析、维氏硬度及拉伸性能测试,研究了冷轧预变形诱发{332}孪晶对Ti-15Mo合金显微组织、ω相析出以及力学性能的影响.结果表明:当冷轧变形量为5％时,预变形诱发孪晶对等温ω相的析出无明
研究了高强高韧Ti-5Mo-5V-6Cr-3Al(TB16)钛合金热穿管的显微组织和力学性能.结果表明:在950℃保温2h通过两棍斜轧穿孔制备高强钛合金管材φ102mm(外径)×φ84mm(内径)×1500mm(长度),显微组织主要由拉长的β相和多边形β相晶粒组成;热穿管经过热处理强化后,抗拉强度不小于1200MPa,屈服强度不小于1100MPa,断后延伸率不小于8％,力学性能优异.