【摘 要】
：
利用静电纺丝法制备了不同煅烧温度和不同La掺杂量的La-TiO2复合纳米纤维。采用SEM和XRD等测试手段对纤维形貌和结构进行了表征。通过对亚甲基蓝MB的光催化降解实验,探讨了La
【机 构】
：
北京服装学院材料科学与工程学院,北京市服装材料研究开发与评价重点实验室,
论文部分内容阅读
利用静电纺丝法制备了不同煅烧温度和不同La掺杂量的La-TiO2复合纳米纤维。采用SEM和XRD等测试手段对纤维形貌和结构进行了表征。通过对亚甲基蓝MB的光催化降解实验,探讨了La的含量和煅烧温度对光催化性能的影响。结果表明:La-TiO2复合纳米纤维催化剂能有效提高催化效率,煅烧温度为600℃,1wt%La含量的La-TiO2复合纳米纤维,在紫外光范围内对有机物(MB)的降解率能够达到77.3%。
La-TiO2 composite nanofibers with different calcination temperatures and different La doping levels were prepared by electrospinning method. The morphology and structure of the fibers were characterized by SEM and XRD. The effects of La content and calcination temperature on photocatalytic activity were investigated by photocatalytic degradation of methylene blue MB. The results show that La-TiO2 composite nanofiber catalyst can effectively improve the catalytic efficiency. La-TiO2 composite nanofibers with a calcination temperature of 600 ℃ and a content of 1wt% La can degrade the organic compounds (MB) in the ultraviolet range to 77.3 %.
其他文献
设计预制体结构参数与织造工艺参数,制备2.5D深交联结构的碳纤维机织物;优化填料配方,采用溶液浸渍、真空辅助相结合的成型工艺,制备出新型深交联结构碳纤维机织物酚醛树脂基
通过添加不同质量分数的二氧化铈(CeO2)纳米粒子,利用相转化法制备锂离子电池隔膜PVDF-HFP/CeO2,所制得的膜通过红外光谱、交流阻抗、线性伏安扫描、首次充放电等方法对其进
以壳聚糖(CTs)﹑马来酸酐(MA)﹑2-丙烯酰胺基-2-甲基丙磺酸(AMPS)为原料,过硫酸铵(APS)为引发剂,N,N’-亚甲基双丙烯酰胺(NMBA)为交联剂,采用紫外光固化的方法合成CTs/AMPS/MA三
采用反相悬浮法,以己二胺为交联剂,将聚琥珀酰亚胺(PSI)分别与三种有机粘土复合,制备了聚天冬氨酸(PAsp)/有机粘土复合吸水性树脂。探讨了有机粘土的种类和含量对复合吸水性
采用戊二醛作为交联剂,采用溶液共混和表面延流法制备壳聚糖/Y2O3/聚丙烯无纺布复合膜。采用IR、DSC、SEM对复合膜进行表面结构表征;对复合膜的结合牢度以及复合膜对磷的吸附
采用潲水油和甲醇为原料,KOH作为催化剂,通过酯交换反应制备生物柴油。综合考察了反应时间、反应温度、催化剂用量、醇油摩尔比和超声波功率5个因素对酯交换反应制备生物柴油
通过静电纺丝的方法制备了单轴取向的聚酰亚胺(PI)纳米纤维膜,并且采用不同环化温度的纳米纤维膜与聚酰亚胺基体进行复合,制备了一种PI纳米纤维增强PI复合薄膜.通过扫描电子
采用静电纺丝技术,以丝素(SF)胶原(COL)混合聚(左旋乳酸-己内酯)(PLCL)制备不同配比的三维纳米纤维支架材料,表征其理化性能并检测细胞相容性,旨为牙周组织工程提供一种新型
以PVC为基体,添加一定量经硅烷偶联剂KH570处理过的石墨,置于自制球磨机中,以100r/min的转速机械球磨30min,在165℃、8MPa的条件下于平板硫化机中热压15min,制备PVC/石墨导电
合成了高等规度的聚丙烯腈(iso-PAN,mm=0.64)和低等规度聚丙烯腈(at-PAN,mm=0.25),并进行了DSC、FT-IR及XRD谱图的研究.研究表明:iso-PAN中-CN基团的反应程度大于at-PAN.