【摘 要】
：
用差热分析和X射线衍射方法,研究了Al_2(WO_4)_3-Na_2O赝二元系相平衡关系。体系中生成两个由包晶反应形成的新化合物2Al_2(WO_4)_3·Na_2O和2Al_2(WO_4)_3·3Na_2O,其包晶反
论文部分内容阅读
用差热分析和X射线衍射方法,研究了Al_2(WO_4)_3-Na_2O赝二元系相平衡关系。体系中生成两个由包晶反应形成的新化合物2Al_2(WO_4)_3·Na_2O和2Al_2(WO_4)_3·3Na_2O,其包晶反应温度分别为800±3℃和682±3℃。化合物2Al_2(WO_4)_3·3Na_2O与Na_2O形成共晶体系,共晶温度592±3℃,共晶点组成为Na_2O73mol％。以Na_2O为助熔剂,长出了Al_2(WO_4)_3:Cr~(3+)的透明单晶体。
The phase equilibrium of Al_2 (WO_4) _3-Na_2O pseudobinary system was studied by differential thermal analysis and X-ray diffraction. In the system, two new compounds 2Al_2 (WO_4) _3 · Na_2O and 2Al_2 (WO_4) _3 · 3Na_2O formed by peritectic reaction were obtained. The peritectic reaction temperatures were 800 ± 3 ℃ and 682 ± 3 ℃ respectively. The compound 2Al_2 (WO_4) _3 · 3Na_2O forms a eutectic system with Na_2O, the eutectic temperature is 592 ± 3 ℃ and the eutectic point is composed of Na_2O73mol%. With Na_2O as flux, a single crystal of Al_2 (WO_4) _3: Cr ~ (3+) was grown.
其他文献
陈思奇(黑)——金磊(白) 这是南方长城杯最后的决赛,印象中这两位棋手是第一次进入全国性大赛的决赛,陈思奇目前是在校大学生,而金磊则是冲段少年,也许,决赛最重要的已经不是
颠覆高校篮坛格局 2004年6月30日晚上,当华中科技大学男篮的小伙子们捧起流光溢彩的金篮板,整个校园变成一片欢腾的海洋时,在体育馆看台的一角,华中科大女篮的队员就象灰姑娘
以上海浦东开发开放为龙头,进而推进长江沿江地区的开发开放,给沿江的九江以及江西全省发展经济带来了极好的机遇。邓小平同志的南巡讲话和中央作出的开放沿江地区的决策,又
本文报导了红外多光子解离二氯一氟甲烷浓集氘的结果。由红外光谱和气相色谱法测得天然丰度原料的含氢化合物的解离速率较含氚化合物的解离速率小约10~4倍。
This paper rep
本文应用正交设计法优化测定条件,用直接发射光谱法测定氧化钕中九种非稀土元素(Pb、Cr、Sn、Sb、Mn、Bi、Co、Ni、zn)。用 NaCl 和 In 分别作为载体和内标准。样品在 Ar 及
研究了在SnCl_2及聚乙烯醇(PVA)存在下用罗丹明B(Rhm B)在水相测定微量铂的高灵敏光度法。其λ_(max)在600 nm处,表观摩尔吸光系数ε_(600)=1.0×10~5l·mol~(-1)·cm~(-1),P
野村俊明等曾研究过四苯卟啉三磺酸(TPPS_5)与Fe(Ⅱ)的显色反应。由于反应速度太慢,需在沸水浴上加热150分钟以上,且共存离子严重影响测定,故未能用于实际样品分析。本文研
身高只有1．88米的哈尔·格瑞尔是76人队历史上最伟大的后卫之一,是在艾弗森之前的另一个费城“小鬼魂”。他最具杀伤力的三件武器是中投、快速灵活的突破和强硬的防守。特别是
利用应变补偿和优化波导结构来提高量子级联激光器的性能,实现了波长为5.5μm量子级联激光器的室温激射.利用双晶X射线衍射实验对材料生长质量进行了检验.对于条宽为20μm,长
Edman降解是蛋白质与肽顺序测定的最常用方法。降解产物经酸性转化后生成各种氨基酸的苯基乙内硫酰脲衍生物(PTH—氨基酸)。鉴定PTH—氨基酸的经典方法有硅胶薄层法;聚酰胺