The effect of ZrO2 content on the performance of vitrified bond was discussed. The results showed that when the ZrO2 content was less than 2 mol%, Zr4+ could enter into the glassy network as mending nets and agglomeration composition. In this case, with the increasing of ZrO2, the vitrified bond’s bending strength increased and the expansion coefficient decreased. It was also found that the wetting angle between the vitrified bond and diamond got small because Zr4+ was enriched on diamond surface. When ZrO2 content was more than 2 mol%, a part of ZrO2 existing in vitrified bond as ZrO2 particles played the role in nucleating agents and promoting the separation of spodumene. When ZrO2 content was 3 mol%, the bending strength of the vitrified bond reached its maximum of 128 MPa and the wetting angle with the diamond reached its minimum of 37.6°.
The effect of ZrO2 content on the performance of vitrified bond was discussed. The results showed that when the ZrO2 content was less than 2 mol%, Zr4 + could enter into the glassy network as mending nets and agglomeration composition. In this case, with the increasing of was ZrO2, the vitrified bond of bending strength increased and the expansion coefficient decreased. It was also found that the wetting angle between the vitrified bond and diamond got small because Zr4 + was enriched on diamond surface. When ZrO2 content was more than 2 mol%, a part of ZrO2 existing in vitrified bond as ZrO2 particles played the role in nucleating agents and promoting the separation of spodumene. When ZrO2 content was 3 mol%, the bending strength of the vitrified bond reached its maximum of 128 MPa and the wetting angle with the diamond reached its minimum of 37.6 °.