TiO2 films were deposited at room temperature by DC pulse magnetron sputtering system.The crystalline structures,morphological features and photocatalytic activity of TiO2 films were systematically investigated by X-ray diffraction(XRD),atomic force microscopy(AFM) and ultraviolet spectrophotometer,respectively.The results indicated that working pressure was the key deposition parameter in?uencing the TiO2 film phase composition at room temperature,which directly affected its photocatalytic activity.With increasing working pressure,the target self-bias decreases monotonously.Therefore,low temperature TiO2 phase(anatase) could be deposited with high working pressure.The anatase TiO2 films deposited with 1.4 Pa working pressure displayed the highest photocatalytic activity by the decomposition of Methyl Orange solution,which the degradation rate reached the maximum(35%) after irradiation by ultraviolet light for 1 h.
TiO2 films were deposited at room temperature by DC pulse magnetron sputtering system. The crystalline structures, morphological features and photocatalytic activity of TiO2 films were systematically investigated by X-ray diffraction (XRD), atomic force microscopy (AFM) and ultraviolet spectrophotometer, respectively. The results indicated that working pressure was the key deposition parameter in? Uencing the TiO2 film phase composition at room temperature, which directly affected its photocatalytic activity. Increasing working pressure, the target self-bias decreases monotonously.Therefore, low temperature TiO2 phase ( anatase could could be deposited with high working pressure. The anatase TiO2 deposited with 1.4 Pa working pressure displayed the highest photocatalytic activity by the decomposition of Methyl Orange solution, which the degradation rate reached the maximum (35%) after irradiation by ultraviolet light for 1 h.