【摘 要】
：
Friction stir processing (FSP),as a new kind of severe plastic deformation technique,can refine and homogenize the microstructure of metallic material.In this study,the effect of FSP on the microstructure and mechanical properties of pure Zr was investiga
【机 构】
：
School of Metallurgical Engineering, Xi’an University of Architecture and Technology, Xi’an 710055,
论文部分内容阅读
Friction stir processing (FSP),as a new kind of severe plastic deformation technique,can refine and homogenize the microstructure of metallic material.In this study,the effect of FSP on the microstructure and mechanical properties of pure Zr was investigated using electron backscatter diffraction analysis,microhardness and room-temperature tensile testing.The fine-grained (FG) structure with an average grain size of～5.3 μtm was obtained in the processed zone,where the average microhardness was ～ 198 HV,1.6 times higher than that of base metal.Furthermore,tensile property of FG pure Zr exhibited obvious anisotropy owing to strong texture.Both grain size and texture had a significant effect on strength and ductility of FG pure Zr.High yield strength (248 MPa) and ultimate tensile strength (483 MPa),as well as good uniform elongation (10％) were achieved,which demonstrated that FSP was an effective method to fabricate bulk FG pure Zr with high strength and good ductility.
其他文献
Friction stir additive manufacturing is a newly developed solid-state additive manufacturing technology.The material in the stirring zone can be re-stirred and reheated,and mechanical properties can be changed along the building direction.An integrated mo
T6-treated 20 wt％ B4Cp/6061Al sheets were joined under welding speeds of 400-1200 mm/min by friction stir welding (FSW) with a threaded cermet pin.The macro-defect-free FSW joints could be achieved at high welding speeds up to 1200 mm/min,but larger plung
W-Y2O3 composite nanopowders prepared via wet chemical method exhibit unique morphologies and microstructures.The yttrium addition during chemical reaction process affects not only the composition of tungsten acid hydrate precursors,but also the reduction
In this work,the influence of the Zener-Hollomon (Z) parameter on the microstructure and mechanical properties of copper subjected to friction stir welding (FSW) was investigated.Liquid N2 cooling was conducted to control the cooling rate after the FSW.Th
X80 pipeline steel plates were friction stir welded (FSW) under air,water,liquid CO2 + water,and liquid CO2 cooling conditions,producing defect-free welds.The microstructural evolution and mechanical properties of these FSW joints were studied.Coarse gran
AA6005A-T6 aluminum hollow extrusions were friction stir welded at a fixed high welding speed of 2000 mm/min and various rotation speeds.The results showed that the heat-affected zone (HAZ) retained the similar grain structure as the base material except
High electromagnetic shielding performance was achieved in the Mg-9Li-3Al-lZn alloy processed by accumulative roll bonding (ARB).The microstructure,electromagnetic interference shielding effectiveness (SE) in the frequency of 30-1500 MHz and mechanical pr
In order to study the effect of friction stir welding (FSW) on corrosion resistance of Al-Cu-Li alloy AA2099-T8,the microstructure and microhardness of FSW joints were characterized,and then,the corrosion behavior of the FSW joints was investigated by the
Dissimilar welded joints of reduced activation ferritic/martensitic (RAFM) steel and 316L austenitic stainless steel were prepared by friction stir welding with different butt joining modes and welding parameters.The weld quality of the joint was improved
Effects of long-term thermal exposure on γ\'particles evolution and impact toughness in the weld joint of Nimonic 263 (N263) superalloy were deeply studied at 750 ℃.Results showed that the precipitates in the weld metal were mainly composed of fine γ\