【摘 要】
：
Four types of steel sheets containing 0.04%, 0.09%, 0.14% and 0.36% Si, respectively, were electrodeposited with a nickel layer of 3 μm in thickness and then g
【机 构】
：
College of Materials Science and Engineering
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Four types of steel sheets containing 0.04%, 0.09%, 0.14% and 0.36% Si, respectively, were electrodeposited with a nickel layer of 3 μm in thickness and then galvanized in molten Zn at 450℃ for various periods of time. The formation and growth of intermetallic compound layers on the surface of the samples were investigated by SEM and EDS. The experimental results show that the method of Ni-electrodeposited pretreatment can distinctively restrain the over-growth of the galvanized coatings of reactive steels and get eligible coatings with a proper thickness, bright appearance and strong adherence. EDS results indicate that a series of Ni-Zn intermetallic compounds γ,γ and δ2 are first formed on the surface of the samples. With a prolonged immersion time, the Г2-Fe-Zn-Ni and δ-Fe-Zn are formed accompanied by the gradual disappearance of γ,γ and δ2 layer. After a longer immersion time, the lumpy ζ- Fe-Zn occurs between δ and liquid Zn and the Г-Fe-Zn does between steel substrate and δ. Subsequently, ζ is in the form of a continuous and compact layer. The method of Ni-electrodeposited pretreatment changes the formation of Fe-Zn intermetallic compounds, which delay the growth of lumpy ζ and promote the growth of compact δ. Consequently, the abnormal growth of reactive steels is eliminated.
其他文献
平板式中温固体氧化物燃料电池(ITSOFC)的密封材料在工作温度下,与其接触的电池材料应具备以下特性:(1)气密性;(2)尺寸稳定性;(3)热匹配性;(4)化学稳定性;(5)绝缘性.采用SiO2
施工项目管理是为使项目实现所要求的质量、所规定的时限、所批准的费用预算,所进行的全过程、全方位的规划、组织、控制与协调.项目管理的目标界定了项目管理的几大控制,即
A novel polyarylene sulflde, polyarylene sulfide sulfone imide, was polymerized with a new monomer (Dichlorodiimide) and sodium sulflde by taking high temperatu
ZnS nano-particles with average sizes of 10 nm and 5 nm were fabricated by sol-gel method, and their pressure-induced phase transformations were in-situ examine
LiNi0.5Mn1.5O4 was prepared under different cooling conditions. The electrochemical properties of LiNi0.5Mn1.5O4 prepared under different cooling conditions wer
Combining with the technology of self-compacting concrete, self-stressing concrete and concrete-filled steel tube, we can get self-compacting and self-stressing
Plasma arc welding was used to join SiCp/Al composite with titanium as alloying filler material. Microstructure of the weld was characterized by an optical micr
Nanosized nickel oxide powders were prepared by thermal decomposition of the nickel citrate gel precursors. The thermal decomposition and powder materials deriv
Spherical Li(Ni1/3Mn1/3Co1/3)O2 was prepared via the homogenous precursors produced by solution spray-drying method. The precursors were sintered at different t
New layered perovskite compounds, AgxNa2-xLa2Ti3O10 (x=0.2, 0.3 and 0.5) were synthesized by an ion-exchange reaction of Na2La2Ti3O10 with AgNO3 solution and ch