The metallic glass matrix composites(MGMCs)and bulk metallic glasses(BMGs)were studied by statistical analysis during plastic deformation at the strain rates of 2×10~(-2),2×10~(-3),and 2×10~(-4) s~(-1),respectively.No serration events occur in both MGMCs and BMGs during compression tests at the strain rate of 2×10~(-2) s~(-1).When deformed at the strain rate of 2×10~(-3) s~(-1),the BMG displays a larger plasticity,which is due to the larger serration events followed by a series of small serrations caused by the continuous movement of free volume.The amplitudes and elastic-energy densities increase with increasing the strain rates owing to many serrations in MGMCs.It is deduced that the Young′s modulus decreases from the normalized stress drop and fluctuations are observed on stressstrain curves,which is attributed to a lower coefficient according to the stick-slip model.
The metallic glass matrix composites (MGMCs) and bulk metallic glasses (BMGs) were studied by statistical analysis during plastic deformation at the strain rates of 2 × 10 -2, 2 × 10 -3, and 2 × 10 ~ (-4) s ~ (-1), respectively.No serration events occur in both MGMCs and BMGs during compression tests at the strain rate of 2 × 10 -2 s -1 .When deformed at the The strain rate of 2 × 10 ~ (-3) s ~ (-1), the BMG displays a larger plasticity, which is due to the larger serration events followed by a series of small serrations caused by the continuous movement of free volume. amplitudes and elastic-energy densities increase with increasing the strain rates due to many serrations in MGMCs.It is deduced that the Young’s modulus decreases from the normalized stress drop and the fluctuations are observed on stressstrain curves, which is attributed to a lower coefficient according to to the stick-slip model.