【摘 要】
：
A novel aqueous Sn-S complex solution was applied as precursor to fabricate SnO2 electron selective layers (ESLs) for the hybrid perovskite solar cells (PSCs). The tin and sulfur powder were directly dissolved in a (NH4)2S water solution to form Sn-S prec
【机 构】
：
State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, School of Materi
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
A novel aqueous Sn-S complex solution was applied as precursor to fabricate SnO2 electron selective layers (ESLs) for the hybrid perovskite solar cells (PSCs). The tin and sulfur powder were directly dissolved in a (NH4)2S water solution to form Sn-S precursor. After depositon and annealing, the SnO2 film was formed, presenting as a low cost and enviromental friendly method for preparation of ESL. The films showed excellent transmittance at visible wavelength range. Moreover, the method exhibited high compatibility for doping using Cu, Cd, Li, and Zn elements. Zn doping (0.05 M) in the as-prepared SnO2 ESL significantly improved perovskite solar cells (PSCs) performance. The highest PCE of 13.17％ was achived with 15％ enhancement compared to that of undoped SnO2 ESL samples. TiCl4 modifications on SnO2 film improved photovoltaic performance to 14.45％, but resulted in the poor long-term stability, around 80％ more degredation than that of PSCs based on Zn-doped SnO2 films.
其他文献
Influences of alkali oxides doping on the crystal structure,defects and hydration behavior of tricalcium silicate C3S were investigated by X-ray powder diffraction with the Rietveld method,inductively coupled plasma optical emission spectroscopy,thermolum
Slow positron beam was applied to study the depth profile structure of the virgin and the aged high-temperature vulcanized silicone rubber (HTV). Scanning electron microscope (SEM) images show that the surface of virgin sample is smooth, while the outdoor
The adventitious carbon located at 284.8 eV was used to calibrate samples without the carbon themselves. When the carbon is as a major part of the inorganic material, the adventitious carbon should be identified and used as the reference. There is no adve
Nanoparticles and microparticles reinforced Al matrix composites were fabricated by spark plasma sintering, and the microstructure and tribological properties were investigated systemically. The nano-Al2O3 particle and micro-Al2O3 particle uniformly dispe
In order to consume the Yellow River sediment as much as possible and improve the longterm stability of the Yellow River,Yellow River sediment was utilized as the main raw material to produce a composite material.Ca(OH)2 was used as alkali-activator to ac
The physical and mechanical properties of self-compacting geopolymer concrete (SCGC)using chemically synthesized nano-geopolymer cement was investigated.Nano-geopolymer cement was synthesized using nano-silica,alkali activator,and sodium aluminate in the
In order to overcome the problem that the low conductivity and high content of graphitic N will lead to serious irreversible capacity loss, magnesiothermic denitriding method was employed to fabricate nitrogen deficient g-C3N4 (ND-g-C3N4). By controlling
The present work presents the microstructure of β-Ca2SiO4 (β-C2S) after accelerated carbonation.The synthesis procedure of β-C2S was examined first,and the crystalline and amorphous structure,the distribution and the pore structure ofβ-C2S carbonation pro
The SnO2 quantum dots (SnO2QDs)/ZnS nanosheets (ZnSNs) heterojunction was fabricated via an in-situ synthetic method at room temperature. Rhodamine B, potassium dichromate, and tetracycline were used to discuss the photocatalytic activities of the as-prep
Nitrogen and sulfur co-doped porous nanocarbon (ZIF-C-N-S) catalyst was successfully synthesized derived from ZIF-8 and thiourea precursors. The electrochemical measurements indicate that the as-obtained ZIF-C-N-S catalyst exhibits higher electrocatalytic