【摘 要】
：
The physical and mechanical properties of self-compacting geopolymer concrete (SCGC)using chemically synthesized nano-geopolymer cement was investigated.Nano-geopolymer cement was synthesized using nano-silica,alkali activator,and sodium aluminate in the
【机 构】
：
Department of Civil and Environmental Engineering, Hanyang University, Seoul 04763, South Korea;Depa
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The physical and mechanical properties of self-compacting geopolymer concrete (SCGC)using chemically synthesized nano-geopolymer cement was investigated.Nano-geopolymer cement was synthesized using nano-silica,alkali activator,and sodium aluminate in the laboratory.Subsequently,nine nano-geopolymer cement sbased SCGC mixes with varying nano-geopolymer cement content,alkali activator content,coarse aggregate (CA) content,and curing temperature were produced.The workability-related fresh properties were assessed through slump flow diameter and slump flow rate measurements.Mechanical performances were evaluated through compressive strength,splitting tensile strength,and modulus of elasticity measurements.In addition,rapid chloride penetration test,water absorption,and porosity tests were also performed.It was assessed that all mix design parameters influenced the fresh and hardened properties of SCGC mixes.Based on test results,it was deduced that nano-geopolymer cement SCGC performed fairly well.All the SCGC mixes achieved the 28-day compressive strength in the range of 60-80 MPa.Additionally,all mixes attained 60％ of their 28-day strength during the first three days of elevated temperature curing.FTIR and SEM analyses were performed to evaluate the degree of polymerization and the microstructure respectively for SCGC mixes.
其他文献
To improve both oxygen evolution efficiency and stability at high temperatures,Mn,Mn+Mo,Mn+Mo+V,and Mn+Fe+V oxide electrodes were prepared on a Ti substrate,with an intermediate layer of IrO2,by an anodic deposition method.The crystal structure,surface mo
Different heating treatments with the variation of heating rates, holding temperatures and holding time were used to simulate the LTPS procedure. The experimental results show that the reheating shrinkage rates of glass substrates are rarely changed with
We fabricated the nanofiber composite membranes by impregnating Nafion into the modified polyvinylidene fluoride(PVDF) electrospinning nanofiber mat for proton exchange membrane fuel cells applications. The hydrophobic PVDF nanofibers mat became to the hy
To investigate the acoustic emission (AE) characteristics of quasi-brittle materials like rock and concrete, and to further analyze their damage and failure mechanism under seismic and other dynamic loads, the uniaxial tension test of granite cylinder spe
In order to develop high-performance diamond wheels, the vitrified bond with different contents of Li2O addition and corresponding diamond composites were prepared. The experimental results show that the addition of a small content of Li2O leads the forma
Influences of alkali oxides doping on the crystal structure,defects and hydration behavior of tricalcium silicate C3S were investigated by X-ray powder diffraction with the Rietveld method,inductively coupled plasma optical emission spectroscopy,thermolum
Slow positron beam was applied to study the depth profile structure of the virgin and the aged high-temperature vulcanized silicone rubber (HTV). Scanning electron microscope (SEM) images show that the surface of virgin sample is smooth, while the outdoor
The adventitious carbon located at 284.8 eV was used to calibrate samples without the carbon themselves. When the carbon is as a major part of the inorganic material, the adventitious carbon should be identified and used as the reference. There is no adve
Nanoparticles and microparticles reinforced Al matrix composites were fabricated by spark plasma sintering, and the microstructure and tribological properties were investigated systemically. The nano-Al2O3 particle and micro-Al2O3 particle uniformly dispe
In order to consume the Yellow River sediment as much as possible and improve the longterm stability of the Yellow River,Yellow River sediment was utilized as the main raw material to produce a composite material.Ca(OH)2 was used as alkali-activator to ac