【摘 要】
：
In order to accelerate the conversion coating formation on 6063 Al alloy in the Ce(NO3)3 solution, accelerants of chloride and ammonium salt were used. The coat
【机 构】
：
School of Materials Science and Engineering,School of Science
论文部分内容阅读
In order to accelerate the conversion coating formation on 6063 Al alloy in the Ce(NO3)3 solution, accelerants of chloride and ammonium salt were used. The coating morphology, composition and structure were analyzed with SEM/EDS, EPMA, XPS and XRD. The coating morphology is influenced by the composition, pH value and temperature of the treating solution. The coating composed of metal oxide, metal hydroxide and hydrate appears to be amorphous. The elements in the coating are Al, Ce, O, Mn and Mg, while the Ce element exists in the forms of Ce3+ and Ce4+. The accelerant of chloride can increase the compactness and Ce content of the coating, so the coating corrosion resistance is remarkably improved. A scheme for the electrochemical reaction in the coating formation was proposed, and the potential change in the coating formation was also studied. It is found that chloride can shorten the time period of the first and the second stages in coating formation.
其他文献
Porous TiAl intermetallic compound, as a novel substitute for current inorganic porous material, offsets the shortages of both ceramics and metals. The environm
Using oxalic acid and stoichiometrically mixed solution of NiCl2, CoCl2, and MnCl2 as starting materials, the triple oxalate precursor of nickel, cobalt, and ma
Ag and Cu filled Chevrel phase MxMo6Te8 (x=1.0, 2.0) samples were synthesized by direct solid state reaction and spark plasma sintering. The electrical and ther
The evolution of texture during the annealing and hot rolling process of extruded AZ31 magnesium alloy sheets was studied. There are two kinds of texture compon
The quality of micro heat pipe(MHP) is strongly affected by sealing technology. Based on the analysis of requirements of sealing technology, a cold welding tech
Ba-Al-S-Eu sputtering target for blue emitting phosphors was prepared by powder sintering method. XRD patterns showed that the main components of the target wer
Effect of Co substitution and annealing treatment on the formation, magnetic properties and microstructure of (NdOyTb)12.3(FeZrNbCu)81.7CoxB6(x=0-15) ribbons pr
Microscopical techniques were used to provide the semi-solid microstructure evolutions of ZK60+RE alloys formed by compression and equal channel angular extrusi
A series of Eu(Ⅲ) complexes of α-thenoyltrifluoroacetone(HTTA) with trioctylphosphine oxide(TPPO) and benzoic acid(BA) or its two derivatives, p-toluic acid(P
The effect of environmental temperature on the damping capacity of Cu-7.66Al-9.52Mn (mass fraction, %) alloy was studied. The result shows that with increasing