Microcasting is one of the significant technologies for the production of metallic micro parts with high aspect ratio(ratio of flow length to diameter).A micro precision casting technology based on investment casting using centrifugal method was investigated.The micro parts of Zn-4%Al alloy with an aspect ratio up to 200 was produced at the centrifugal speed of 1 500 r/min and the mold temperature of 270℃.The investigations on the relationship between flow length and rotational speed were carried out. For microcasting,the flow length is not only dependent on the centrifugal speed under the constant centrifugal radius,but also on the preheating temperature of mold.The flow length increases as the rotational speed and the mold temperature increase,and is much higher at a mold temperature of 270 ℃thanat other mold temperatures.
Microcasting is one of the significant technologies for the production of metallic micro parts with high aspect ratio (ratio of flow length to diameter). A micro precision casting technology based on investment casting using centrifugal method was investigated. The micro parts of Zn-4% Al alloys with an aspect ratio up to 200 was produced at the centrifugal speed of 1 500 r / min and the mold temperature of 270 ° C. The investigations on the relationship between flow length and rotational speed were carried out. For microcasting, the flow length is not only dependent on the centrifugal speed under the constant centrifugal radius, but also on the preheating temperature of the mold. The flow length increases and the mold temperature increase, and is much higher at a mold temperature of 270 ° C thanat other mold temperatures.