【摘 要】
：
本文利用纤维测强法研究了镀铝SiC(Ti)纤维经不同规范热处理后的抗拉强度变化规律,探讨了SiC(Ti)纤维与铝的相容性。采用超声液相浸渗法成功地制备出SiC(Ti)/Al预制丝。预制
【机 构】
：
国防科技大学材料工程与应用化学系,国防科技大学材料工程与应用化学系,国防科技大学材料工程与应用化学系,国防科技大学材料工程与应用化学系
论文部分内容阅读
本文利用纤维测强法研究了镀铝SiC(Ti)纤维经不同规范热处理后的抗拉强度变化规律,探讨了SiC(Ti)纤维与铝的相容性。采用超声液相浸渗法成功地制备出SiC(Ti)/Al预制丝。预制丝强度及其萃取纤维强度试验和金相、扫描电镜观察等结果表明,该纤维在所定的工艺条件下强度降级甚小,纤维与铝之间的结合良好,所制出的预制丝强度达到ROM预测值。
In this paper, the change of tensile strength of aluminized SiC (Ti) fibers after heat treatment under different specifications was studied by fiber strength test, and the compatibility between SiC (Ti) fibers and aluminum was discussed. SiC (Ti) / Al preform was successfully prepared by ultrasonic liquid infiltration method. The results of the prestressing yarns, the strength of the extracted fibers and the metallographic and scanning electron microscope observations showed that the strength of the fibers was very small and the bonding between fiber and aluminum was good. The strength of the prepared yarns reached ROM predicted value.
其他文献
用ab-initio法对硅氧烷及硅酸分子的研究指出,在硅酸盐中,由于电子的局域性,体系的总能量可以向结构单元或双中心分割:从而可以得到Si-O~(br)比Si-O~(ter)更稳定。用这些结果
当飞机变旧时,座舱增压循环会导致紧固件和风挡周围产生裂纹。常规裂纹修补方法劳动强度较大,耗费时间较多。此外,还要求能够处理一系列与修补有关的维护问题。目前,由美国
为了了解无压烧结 Si_3N_4基陶瓷材料(下称 Si_3N_4基陶瓷)的抗磨损性能,以便在工业中得到应用,用环块磨损试验机对 Si_3N_4基陶瓷—金属摩擦副进行了磨损试验。试验结果表明
采用X射线衍射、X射线能谱,Mossbauer谱,对比地分析了6063合金和加入微量混合稀土的R.E6063合金的金相相组成。结果表明:6063和R.E6063合金都有α(Al),Mg_2Si,FeAl_3,(AlFeSi
用薄膜X射线衍射、扫描电镜、透射电镜和X光光电子能谱(XPS)技术对经350～540℃/30分～240分氧化处理的Co基(Mn、Mo、Fe、Si、B)非晶合金的表面组织、结构及状态的变化进行了研究
本文用X射线、金相显微镜、扫描电镜、能谱、振动样品磁强计和磁称等方法,研究了R(Fe,M)_12(R为稀土元素,M为Ti,V)的晶体结构、微观组织和磁性。发现RFe_(10)Ti(除Nd外)的铸
小学生的综合能力的培养是指“学生听、说、读、写的能力的培养。”语文重在实践,实践源于学生的语文综合能力,能力的培养离不开课堂教学的主阵地,为了培养学生的语言文字运
金属基复合材料可以为轻金属结构提供极好的机械性能。然而,直到最近,这些高性能的材料并没有找到很多主要的工业应用市场,大部分原因是由于它们的制造成本太高。现在研制成
以15％富铝红柱石晶须增强氧化铝,断裂强度达15MPa/m~2,比未增强时提高100％。最近报道了几种富铝红柱石的增强方法,最为人们感兴趣的是用汽相反应产生铝红柱石晶须的方法。铝红
利用电子能量损失谱、微衍射及高分辨电子显微术等方法观察和分析了直径为5—30nm的超细羰基铁粉和直径为30—80nm 的 SiCB 超细粉。超细铁粉主要由中心核α-Fe 和外壳 Fe_3O