【摘 要】
：
以15％富铝红柱石晶须增强氧化铝,断裂强度达15MPa/m~2,比未增强时提高100％。最近报道了几种富铝红柱石的增强方法,最为人们感兴趣的是用汽相反应产生铝红柱石晶须的方法。铝红
论文部分内容阅读
以15％富铝红柱石晶须增强氧化铝,断裂强度达15MPa/m~2,比未增强时提高100％。最近报道了几种富铝红柱石的增强方法,最为人们感兴趣的是用汽相反应产生铝红柱石晶须的方法。铝红柱石晶须在提高刚性的同时,还提高了氧化锆基体的高温机械性能。为了接近全密度,要求该复合材料体系的燃烧温度比未增强氧化锆提高150℃,在1400℃燃烧。
Alumina reinforced with 15% mullite whiskers, the breaking strength of 15MPa / m ~ 2, 100% higher than the non-enhanced. Recently, several methods for enhancing mullite have been reported, and the most interesting one is the method of producing mullite whisker by vapor phase reaction. The mullite whisker improves the high temperature mechanical properties of the zirconia matrix while improving the rigidity. In order to achieve full density, the composite system is required to have a combustion temperature that is increased by 150 ° C than that of the non-reinforced zirconia and burned at 1400 ° C.
其他文献
一、前言 众所周知,Fe-B-Si系非晶合金具有优异的软磁性,用作变压器铁芯,铁芯损耗仅为硅钢片铁芯的1/4～1/5,因而可大量节约能源。但由于Fe-B-Si系非晶态合金与其它非晶合金一
近几年,我国司法实践在审理保险案件时出现了一种倾向:尽量判决保险公司赔偿。这种倾向产生了一个很不好的后果:骗保事件大量发生。有数字统计,在北京汽车保险市场上,骗赔率
用ab-initio法对硅氧烷及硅酸分子的研究指出,在硅酸盐中,由于电子的局域性,体系的总能量可以向结构单元或双中心分割:从而可以得到Si-O~(br)比Si-O~(ter)更稳定。用这些结果
当飞机变旧时,座舱增压循环会导致紧固件和风挡周围产生裂纹。常规裂纹修补方法劳动强度较大,耗费时间较多。此外,还要求能够处理一系列与修补有关的维护问题。目前,由美国
为了了解无压烧结 Si_3N_4基陶瓷材料(下称 Si_3N_4基陶瓷)的抗磨损性能,以便在工业中得到应用,用环块磨损试验机对 Si_3N_4基陶瓷—金属摩擦副进行了磨损试验。试验结果表明
采用X射线衍射、X射线能谱,Mossbauer谱,对比地分析了6063合金和加入微量混合稀土的R.E6063合金的金相相组成。结果表明:6063和R.E6063合金都有α(Al),Mg_2Si,FeAl_3,(AlFeSi
用薄膜X射线衍射、扫描电镜、透射电镜和X光光电子能谱(XPS)技术对经350～540℃/30分～240分氧化处理的Co基(Mn、Mo、Fe、Si、B)非晶合金的表面组织、结构及状态的变化进行了研究
本文用X射线、金相显微镜、扫描电镜、能谱、振动样品磁强计和磁称等方法,研究了R(Fe,M)_12(R为稀土元素,M为Ti,V)的晶体结构、微观组织和磁性。发现RFe_(10)Ti(除Nd外)的铸
小学生的综合能力的培养是指“学生听、说、读、写的能力的培养。”语文重在实践,实践源于学生的语文综合能力,能力的培养离不开课堂教学的主阵地,为了培养学生的语言文字运
金属基复合材料可以为轻金属结构提供极好的机械性能。然而,直到最近,这些高性能的材料并没有找到很多主要的工业应用市场,大部分原因是由于它们的制造成本太高。现在研制成