【摘 要】
：
CuZnAl catalysts with different La loadings were prepared by a complete liquid phase method and tested for higher alcohols (C2+OH) synthesis from syngas at the conditions of 250-290 ℃,4.SMPa,feed low rate=150mL/min and H2/CO=2.The catalysts were character
【机 构】
：
Key Laboratory of Coal Science and Technology of Ministry of Education and Shanxi Province, Taiyuan
论文部分内容阅读
CuZnAl catalysts with different La loadings were prepared by a complete liquid phase method and tested for higher alcohols (C2+OH) synthesis from syngas at the conditions of 250-290 ℃,4.SMPa,feed low rate=150mL/min and H2/CO=2.The catalysts were characterized by XRD,H2-TPR,NH3-TPD,N2 adsorption,XPS,and TEM techniques.Characterization results showed that the incorporation of La into CuZnAl catalysts resulted in the decrease of crystallite size of Cu0 and a strong interaction among copper and zinc or aluminum oxides.Especially,the incorporation of La increased the amount of weak acid and the Cu content on catalyst surface,which was speculated to contribute the formation of higher alcohols.Among these La-promoted CuZnAl catalysts,the La0.1 catalyst exhibited the best catalytic performance and the selectivity to higher alcohols reached above 60％ when the reaction temperature was 290 ℃.
其他文献
Herein,we report visible light active mesoporous cadmium bismuth niobate (CBN) nanospheres as a photocatalyst for hydrogen (H2) generation from copious hydrogen sulfide (H2S).CBN has been synthesized by solid state reaction (SSR) and also using combustion
Herein,we reported in situ synthesis of biomass-derived Ni/C catalyst by self-reduction with pomelo peel.Compared with the conventional method,which includes carbonization,activation,impregnation and reduction,the entire preparation process was simplified
Cux-Fey/SiO2 catalysts were prepared using urea-assisted sol-gel method.The structure and physicochemical properties of the catalysts were characterized using N2 adsorption-desorption,transmission electron microscopy,H2-temperature-programmed reduction,po
The capacity to capture CO2 was determined in several stoichiometric compositions in the Li2O-Bi2O3 system.The compounds (Li7BiO6,Li5BiOs,Li3BiO4 and LiBiO2 phases) were synthesized via solid-state reaction and characterized by X-ray diffraction,scanning
High-quality graphene flakes have long been desirable for numerous applications including energy storage,printable electronics,and catalysis.In this contribution,we report a green,efficient,facile gas-driven exfoliation process for the preparation of high
The key point in CO2 methanation is to improve the activity at low temperature and the stability.For this purpose,a new cerium-modified Ni-La2O3/ZrO2 catalyst was prepared using La1-xCexNiO3/ZrO2 with perovskite phase as the precursor,which was obtained b
The cycle life of oxygen carrier (OC) is crucial to the practical applications of chemical looping combustion (CLC).Cycle performance of Cu/SiO2 prepared with a mechanical mixing method was evaluated based on a CLC process characterized with an added meth
Three different regeneration processes including hydrogen or nitrogen purging and coke-burning treatment were used to restore the Pt-Sn/γ-Al2O3 catalysts,through which propane dehydrogenation reaction was performed in a consecutive reaction-regeneration m