【摘 要】
：
The influences of solidification rate on the microstructures of cast strips and corresponding sintered NdFeB magnets were investigated. The experimental results
【机 构】
：
National Engineering Research Center for Rare Earth Materials
论文部分内容阅读
The influences of solidification rate on the microstructures of cast strips and corresponding sintered NdFeB magnets were investigated. The experimental results show that the volume fraction and size of columnar grains vary with the wheel speed V, and the fraction is highest to more than 90% with 3.5 μm in average width at V＝2 m·s-1. The reasons for the improved magnetic performance were discussed based on the micromagnetic theory and microstructure analyses of the strips and sintered magnets. The magnetic properties of sintered NdFeB magnets made from the (Nd,Dy)13.0(Fe,Ga,Al)80.5B6.5 cast strip which was obtained at V=2 m·s-1 are as follows: Br=1.15 T(11.25 kG), iHc=2799 kA·m-1 (35.2 kOe) and (BH)max=242 kJ·m-3(30.35 MGOe).
其他文献
The experiments of continuous and directional solidification of titanium alloys with cold crucible were carried out in a multifunctional electromagnetic cold cr
Rapid solidification method was employed to produce TiAl based alloy ribbons and finally to produce TiAl based alloys with novel microstructure and properties.
Polycrystalline bulk Ti3AlC2 material with high purity and density was fabricated by hot pressing from the powder mixture with the starting stoichiometric mole
As-cast AZ91+XCa (X=0, 0.5%, 1.0%, 1.5%, mass fraction) magnesium alloys were extruded into tube at 380℃ with an extrusion ratio of 6:1. The tensile properties
The true stress-strain curves of compressed ZK60 alloy have two typical characters. Most thermal simulation compressing curves of ZK60 have the obvious characte
Alloying is an important method to improve properties of casts. The influences of Mo and RE on the mechanical properties of ZG30Cr were investigated in this wor
The effects of carbon on the microstructure and mechanical properties of DD99 single crystal superalloy were investigated. The results show that stress rupture
Hafnium carbide (HfC) was applied in space and aerospace due to its ultra high melting temperature, high specific strength and moderate oxidation resistance. A
The diffusion behaviors of helium atoms at two symmetric grain boundaries (Σ5{210} and Σ3 {112}) of Pd were investigated using molecular dynamics simulations
C + ion beam-assisted deposition was utilized to prepare deposit diamond-like carbon (DLC) film.With the help of a series of experiments such as Raman spectrosc