【摘 要】
：
The experiments of continuous and directional solidification of titanium alloys with cold crucible were carried out in a multifunctional electromagnetic cold cr
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
The experiments of continuous and directional solidification of titanium alloys with cold crucible were carried out in a multifunctional electromagnetic cold crucible apparatus. Parameters and factors influencing the surface crack and macrostructure of titanium alloy ingots were studied. The mechanism of the parameters and factors influencing the surface crack and macrostructure of the ingots were interpreted. The results show that the surface cracks of the prepared ingots decrease with the increase of the input power from 50 to 60 kW or with the increase of the coil turns from 3 to 5 circles. The surface cracks increase with the increase of withdrawal velocity from 3 to 5 mm/min or the height of the primer from 2 to 3 cm, then decrease with the increase of withdrawal velocity from 5 to 8.7 mm/min or the height of the primer from 3 to 4 cm. Coil turns is the most important one in all parameters effect on the surface crack, the input power is more important, then the withdrawal velocity is important and the height of the primer is the least important. Withdrawal velocity is the most important factor affecting the macrostructure, and effects of other factors on macrostructure is slight. With the decrease of velocity from 8.7 to 0.5 mm/min, the quantity of grains reduces, the grain orientation degree becomes small, and the solidification fronts change from concave to plane to convex. The ingot can be directional solidified at velocity of 1 mm/min. The ingot with free surface crack and directional macrostructure is prepared under definite conditions.
其他文献
The powder mixture of Cu and graphite was mechanically alloyed (MA) in an oscillating type ball mill. The milling time was varied in order to investigate its in
AgGa1-xInxSe2 polycrystals were synthesized by the method of mechanical oscillation and temperature oscillation. X-ray diffraction spectra of polycrystal powder
Ramie cloth/UP resin composite was formed at 0.2 MPa and cured at room temperature for 24 h and treated at 80 ℃ for2 h. The physical and mechanical properties
In this work, we present an evaluation of the performance and error robustness of RTP-based broadcast streaming of high-quality high-definition (HD) H.264/AVC v
The microstructure of the as-cast, as-solution-treated and as-aged wrought magnesium alloy ZK60 was studied. The results indicate that the microstructure of the
The effects of heat treatment on the microstructure and compressive properties of porous Ni-rich NiTi shape memory alloy (SMA) fabricated by self-propagating hi
The springback is one of the key factors which affect the forming quality of thin-walled tube NC precision bending. The elastic-plastic finite element method wa
For developing high performance magnesium alloys, a new method in combination of B2O3 addition and melt stirring was applied. When 0, 3%, 6% and 12%( mass fract
The deformation and damage mechanism of aluminum alloy (6063) were investigated by 0°, 30°, 45°, 60° and 90° tensile tests and tensile-unload tests with th
The effect of 5%Cr(mole fraction) on the scaling behavior of Ni-10Al was investigated at 900 ℃ and 1 000 ℃ with the aim to discuss the third element effect(TE