The study on the effects of SrO/Al 2O 3 molar ratio on the crystalline phases and photoluminescence characteristics of strontium aluminate phosphors co-activated with Eu 2+ and Dy 3+ were conducted by X-ray powder diffractometry, fluorescence spectrometer and photometer. The strontium aluminate luminescent materials with different SrO/Al 2O 3 molar ratio emit the visible lights with different color tone after removal of excitation. The peak wavelengths of the emission spectra drift in the direction of short wave, the quantity of Sr 4Al 14O 25 crystalline phase increases and the afterglow time lengthens with the SrO/Al 2O 3 reduction. The results show that when the SrO/Al 2O 3 molar ratio is near 1, the photoluminescence materials have high luminescent intensity, and when it is near 0.75, they have long afterglow time. However, when SrO/Al 2O 3 molar ratio is more than 1, the luminescent materials appear strong alkaline in water solution; when SrO/Al 2O 3 molar ratio is much less than 0.75, the samples need a higher temperature to be sintered.
The study on the effects of SrO / Al 2 O 3 molar ratio on the crystalline phases and photoluminescence characteristics of strontium aluminate phosphors co-activated with Eu 2+ and Dy 3+ were by X-ray powder diffractometry, fluorescence spectrometer and photometer. The strontium aluminate luminescent materials with different SrO / Al 2 O 3 molar ratio emit the visible lights with different color tone after removal of excitation. The peak wavelengths of the emission spectra drift in the direction of short wave, the quantity of Sr 4Al 14O 25 crystalline phase increases and the afterglow time lengthens with the SrO / Al 2 O 3 reduction. The results show that when the SrO / Al 2 O 3 molar ratio is near 1, the photoluminescence materials have high luminescent intensity, and when it is near 0.75, they have long Afterglow time. However, when SrO / Al 2 O 3 molar ratio is more than 1, the luminescent materials appear strong alkaline in water solution; when SrO / Al 2 O 3 molar ratio is much less than 0.75, the samples need a higher temperature to be sintered.