【摘 要】
：
A low-cost and efficient filter medium for Cd(II) removal was prepared by anchoring -SCN functional groups (by 3-thiocyanatopropyltriethoxysilane, TCPS) on ceramsite via the approach of synthesizing a honeycomb calciumaluminum-silicate-hydrate (C-A-S-H) l
【机 构】
：
State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, Wuhan
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
A low-cost and efficient filter medium for Cd(II) removal was prepared by anchoring -SCN functional groups (by 3-thiocyanatopropyltriethoxysilane, TCPS) on ceramsite via the approach of synthesizing a honeycomb calciumaluminum-silicate-hydrate (C-A-S-H) layer as intermediate. The specific surface area of ceramsite was increased enormously by more than 50 times because of the modification of honeycomb layer. Moreover, the abundant Si-OH bonds existing in the structure of CAS-H can serve as active sites for TCPS. The combined effects ensure that the hybrid filter medium (named ceramsite/C-A-S-H/TCPS) demonstrated a high Cd(II) adsorption capacity of 18.27 mg·g1 for particle size of 0.1-0.6 mm, 12.63 mg·g-1 for 0.6-1.25 mm and 8.64 mg g-1 for 1.25-2.35 mm. The Cd(II) adsorption capacity per unit area of ceramsite/C-A-S-H/TCPS (0.1-0.6 mm) is up to 4.07 mg·m-2, which is much higher than that of many nano-adsorbents. In addition, ceramsite/C-A-S-H/TCPS could maintain a high removal efficiency (> 85%) in a wide range of pH 3-11 and showed excellent selectivity in the presence of competing ions. Furthermore, Cd(II) could be desorbed from ceramsite/C-A-S-H/TCPS composites with nearly 100%, suggesting the potential application in recycling of heavy metal ions.
其他文献
Transparent hydroxyapatite (HAp) ceramics with the grain size ranging 86-1 300 nm were successfully synthesized by spark plasma sintering (SPS) at 925-1 200 ℃.All the sample achieved final density higher than 99.7％.The phase stability was identified by X-
To promote the stability and efficiency, quadruple-cation perovskite system (blending of MA, FA, Cs, I, Br, etc) was introduced to substitute the traditional MAPbI3 perovskite. Perovskite films degraded by water can be recovered by a simple method. The Pb
The present study aimed to improve the pervaporation (PV) performances of polydimethy-lsiloxane (PDMS) membranes by using special cross-linkers. The γ-methacryloxypropyl trimethoxy silane (KH-570) cross-linked PDMS membranes were fabricated and characteri
Based on the mechanical properties and microstructure of polyurethane foam solidified material, a two-dimensional model of polyurethane foam solidified material was constructed. Polyurethane foam was obtained by fully and uniformly mixing the two componen
A citrate-assisted hydrothermal method was utilized for the preparation of Sr-substituted hydroxyapatite (HA) nanoparticles. The influences of Sr-substituting degree on the phase identifications, microstructures and colloidal stability of the resultant pr
Fly ash (FA) was utilized to hydrothermally synthesize FA based Al-substituted tobermorites, and was combined with raw materials of FA and municipal solid waste incineration fly ash (MSWI) to hydrothermally synthesize FA-MSWI based Al-substituted tobermor
In order to reflect truly the damage evolution mechanism of weak muddy intercalation in dry-wet cycles, two typical weak muddy intercalations were selected for dry-wet cycles. The mineral changes of specimens were analyzed via X-ray diffraction after dry-
The bovine hydroxyapatite (BHA) was applied to prepare biological tissue engineering scaffolds by the method of extrusion freeforming.To achieve this goal,BHA were added to sodium alginate (SA) solution to form a slurry system in appropriate proportion.Th
Mg/Ni hybrid foams were fabricated by the electroless method. The Ni-P (Nickel-Phosphorous) coatings were deposited on the surface of closed-cell Mg alloy foams. The composition, microstructure and phases of the Ni-P coatings were characterized by scannin
Ti(C,N)-TiB2 cermets were fabricated from Ti(C,N), TiB2, Co and WC powder mixtures via a vacuum hot pressing process. The influence of TiB2 content on their microstructures and mechanical properties was investigated. As a result of the elevated TiB2 conte