An oxidation resistant Al-Cu-Fe quasicrystalline coating was fabricated on substrate of Ti alloy by low pressure plasma spraying (LPPS) method. As-sprayed Al-Cu-Fe coating has a rapidly solidified lamellar microstructure consisting of quasicrystalline phase and crystalline phase. The formation of quasicrystalline coating is related to the annealing. The results from the ox!dat!on experiments showed that Al-Cu-Fe quasicrystalline coating improved the oxidation resistance of Ti-base alloys. During the oxidation period there is no evident spallation of the coating from the substrate. Oxide formed on the surface of Al-Cu-Fe quasicrystalline coating after oxidation consisted of Al2O3. Oxidation occurs Ieading to a change of concentration and phase transformation in the coating surface. Selective oxidation of AI transforms the quasicrystalline phase into the phase.
An oxidation resistant Al-Cu-Fe quasicrystalline coating was fabricated on substrate of Ti alloy by low pressure plasma spraying (LPPS) method. As-sprayed Al-Cu-Fe coating has a rapidly solidified lamellar microstructure consisting of quasicrystalline phase and crystalline phase. The formation of quasicrystalline coating is related to the annealing. The results from the ox! Dat! On experiments showed that Al-Cu-Fe quasic crystalline coating improved the oxidation resistance of Ti-base alloys. The coating from the substrate. Oxide formation on the surface of Al-Cu-Fe quasic crystalline coating after oxidation consisted of Al2O3. Oxidation occurs Ieading to a change of concentration and phase transformation in the coating surface. Selective oxidation of AI transforms the quasicrystalline phase into the phase.