The embedded atom method (EAM) was used to theoretically analyze the effect of the lattice parameter variation on the order-disorder transformation in binary alloys. Based on EAM, it is found that only one kind of order-disorder transition (second- order transition) exists for AB alloy. Three groups of order-disorder transformation can be observed for the A3B or AB3 compounds. For group I, the order-disorder is a completely first-order transition. For group II, the order-disorder transformation is a classical first-order transition. For group III, the order-disorder transformation is found to be a second-order transition. The lattice parameter variations have a significant effect on E2 coefficient, which is related to the ordering energy. These results are in good agreement with experiments.
The embedded atom method (EAM) was used to theoretically analyze the effect of the lattice parameter variation on the order-disorder transformation in binary alloys. Based on EAM, it is found that only one kind of order-disorder transition (second- order transition Three groups of order-disorder transformation can be observed for the A3B or AB3 compounds. For group I, the order-disorder is a completely first-order transition. For group II, the order-disorder transformation is a classical first-order transition. For group III, the order-disorder transformation is found to be a second-order transition. The lattice parameter variations have a significant effect on E2 coefficient, which is related to the ordering energy. These results are in good agreement with experiments.