【摘 要】
：
通过在2.8C-31Cr合金中添加Ti、V、Nb、Mo制备多元铬系合金,研究了Ti、V、Nb、Mo的添加对高铬合金碳化物形态、硬度和冲击韧度的影响。结果表明,随着合金元素加入量的增加,高
【机 构】
：
四川理工学院机械工程学院,西安建筑科技大学,
论文部分内容阅读
通过在2.8C-31Cr合金中添加Ti、V、Nb、Mo制备多元铬系合金,研究了Ti、V、Nb、Mo的添加对高铬合金碳化物形态、硬度和冲击韧度的影响。结果表明,随着合金元素加入量的增加,高铬合金凝固组织中碳化物尺寸先细化到粗化,硬度和冲击韧度先增加后降低。加入0.4%的Ti、0.4%的V、0.4%的Nb、0.4%的Mo时,高铬合金的铸态组织和综合力学性能最好,硬度(HRC)为58.9,冲击韧度为11J·cm-2。
The effects of addition of Ti, V, Nb and Mo on the carbide morphology, hardness and impact toughness of high chromium alloy were investigated by adding Ti, V, Nb and Mo to 2.8C-31Cr alloy. The results show that with the addition of alloying elements, the size of carbide in the solidified structure of the high chromium alloy is first refined to coarseness, and the hardness and impact toughness first increase and then decrease. When 0.4% Ti, 0.4% V, 0.4% Nb and 0.4% Mo are added, the as-cast microstructure and mechanical properties of the high-chromium alloy are the best, the HRC is 58.9 and the impact toughness is 11J · cm -2.
其他文献
采用传统钨极电弧真空熔炼技术制备了NiTiCu形状记忆合金.通过光学显微镜、X射线衍射分析、接触角测试、硬度测试及电化学工作站,对铸态NiTiCu合金的金相组织形貌、相组成、
采用铜型铸造法制备直径为12mm的Ti35Zr30Be27.5-xCu7.5Cox(x=3.5,7.5,11.5)系列块体非晶合金。采用X射线分析(XRD)、差示扫描量热仪(DSC)研究了Co元素含量变化对Ti-Zr基合金
研究了填料(铁粉和铝粉)含量对E-44环氧树脂背衬材料力学性能的影响。结果表明,铁粉与E-44的质量比为(3~4.2)∶1,铝粉与E-44的质量比为(2~3.2)∶1时,能获得均匀的背衬材料,其
在医院感染的预防、控制中,护理工作担当着重要的任务,非典后我们对护理工作中引发医院感染的薄弱环节进行追踪监测,并制订了相应的对策,取得了一定的成效,现总结如下。
目的探讨马来酸曲美布汀片联合美常安胶囊治疗肠易激综合征的疗效。方法将151例肠易激综合征患者随机分为3组,A组服用马来酸曲美布汀片和美常安胶囊,B组只服用马来酸曲美布汀
基于Three Dimensional Atom Probe(3DAP)以及First-Principles对Al-Si-Cu-Mg合金中团簇及后续沉淀的演变过程进行了研究。3DAP试验表明,Al-1.0Si-1.5Cu-0.5Mg合金时效0.25h
手术患者在手术室停留的时间虽然短暂,但却是整个疾病治疗中关键的一环,而且在此期间患者将与其亲属分别,独立面对陌生的手术环境、紧张气氛,给患者带来一定的紧张与恐惧会直接影响手术的顺利进行及术后康复.我院2006年开始在手术室应用人性化护理,取得了满意的效果,报告如下。
2016年7月16-18日,中国医学装备协会第25届学术年会在贵阳隆重举行。作为中国医学装备协会的分支机构,医用机动车辆装备技术专业委员会(以下简称“专委会”)同期组织召开了20
采用再结晶与重熔法制备了2024铝合金半固态坯料,研究了不同重熔温度和保温时间下坯料的微观组织演变,以及工艺参数对晶粒尺寸和球化程度的影响。通过触变挤压铸造成形试验,
在原位Mg2Si/Al复合材料中,通过P和混合稀土复合变质及改变半固态等温热处理的保温温度和保温时间,研究了复合变质及等温热处理对合金组织与力学性能的影响。结果表明,P和混