【摘 要】
：
The effect of sulphide (Na2S) concentration (SC) on the corrosion and cavitation erosion behaviours of a cast nickel aluminium bronze (NAB) in 3.5％ NaC1 solution is investigated in this study.The results show that when the SC exceeds 50 ppm,the hydrogen e
【机 构】
：
College of Mechanical and Electrical Engineering, Hohai University, 200 Jinling North Road, Changzho
论文部分内容阅读
The effect of sulphide (Na2S) concentration (SC) on the corrosion and cavitation erosion behaviours of a cast nickel aluminium bronze (NAB) in 3.5％ NaC1 solution is investigated in this study.The results show that when the SC exceeds 50 ppm,the hydrogen evolution reaction dominates the cathodic process,and a limiting current region appears in the anodic branch of the polarisation curve due to the formation of a copper sulphide film,which is a diffusion-controlled process.After longterm immersion,the increased mass loss rate of NAB with the sulphide additions of 20 and 50 ppm is attributed to the less protective films,which contains a mixture of copper oxides and sulphides.Moreover,NAB undergoes severe localised corrosion (selective phase corrosion,SPC) at the β\'phases and eutectoid microstructure α + κⅢ.By comparison,NAB undergoes general corrosion and a copper sulphide film is formed in 100 and 200 ppm sulphide solutions.Cavitation erosion greatly increases the corrosion rate of NAB in all solutions and causes a negative potential shift in 3.5％ NaC1 solution due to the film destruction.However,a positive potential shift occurs in the solutions with SC higher than 50 ppm due to the accelerated mass transfer of the cathodic process.The cavitation erosion mass loss rate of NAB increases with the increase of SC.The occurrence of severe SPC decreases the phase boundary cohesion and causes brittle fracture under the cavitation impact.The corrosion-enhanced erosion is the most predominant factor for the cavitation erosion damage when the SC exceeds 50 ppm.
其他文献
The pure Zn foils with different thicknesses (0.02,0.05,0.1,0.2 and 0.3 mm) were selected as interlayers to improve the quality of friction stir lap welding joint of 7075-T6 Al and AZ31B Mg dissimilar alloys.The effects of the interlayer thickness on join
Fabrication of ternary Nb-17Si-23Ti alloys was attempted by in situ reaction laser melting deposition (LMD) with dual powder feeding method from Nb-28 at.％ Ti powder mixture and pure Si powder.The microstructures of the asdeposited alloys were examined wi
Carbon nanotube (CNT)-reinforced 6061Al (CNT/6061Al) composites were fabricated via powder metallurgy combined with friction stir processing (FSP).CNTs were dispersed after FSP and accelerated the precipitation process of the CNT/6061Al composites.However
Glass fibres/epoxy resins composites have been performed as ideal materials to make support instruments for high-energy and nuclear physics experiments.The effects of the γ-ray irradiation on the fatigue strength,thermal conductivities and thermal stabili
Boron-doped aluminum nitride (B-A1N) thin films were synthesized on A1 substrates by using chemical vapor deposition method by changing the synthesis parameters and were used as thermal interface material for high power light emitting diode (LED).The B-A1
Solidification shrinkage has been recognized as an important factor for macrosegregation formation.An arbitrary Lagrangian-Eulerian (ALE) model is constructed to predict the macrosegregation caused by thermal-solutal convection and solidification shrinkag
Mixtures of W and B13C2 powders were mechanically milled and subsequently annealed at 900-1200℃.It is found that amorphous W-B-C alloy formed as the mixtures were milled for 20-80 h.After annealing the 80 h-milled mixtures at 900-950 ℃,solid solutions of
Target assembly is a key consumable material for producing thin film used in the electronic packaging and devices.The residual stresses induced during the process of soldering are detrimental to the performance of target assembly.In this work,the intensit
Mg-Zn-Ag alloys have been extensively studied in recent years for potential biodegradable implants due to their unique mechanical properties, biodegradability and biocompatibility. In the present study, Mg-3Zn-xAg (wt％, x = 0. 2, 0. 5 and 0. 8) alloys wit
Both of the single crystal (SX) castability and undercoolability of PWA 1383 superalloy were investigated during the directional solidification and isothermal cooling.In all the six SX parts of a casting cluster,no stray grains were found,revealing a defe