The effects of ultrasonic vibration on the grain size and morphology of Mg2Si in Mg-4 wt% Al-1 wt%Si(AS41) alloys designed were evaluated. The results show that the major constituents of the alloy include β-Mg17Al12 and Mg2Si phase, and no difference in the type of constituents between without ultrasonic vibration and with ultrasonic vibration. Without any ultrasonic vibration, the grain size and Mg2Si phase in AS41 alloy are coare structure. However, the microstructure with fine uniform grains and Mg2Si particles are achieved with ultrasonic vibration. The crystal grains and Mg2Si particles refine with increase in the ultrasonic vibration intensity. When the ultrasonic vibration intensity was too low or too high, coarse structures could be obtained. The analysis of refinement mechanism indicates that the acoustic cavitation and flows induced by ultrasonic vibration lead to the fine uniform microstructure.
The effects of ultrasonic vibration on the grain size and morphology of Mg2Si in Mg-4 wt% Al-1 wt% Si (AS41) A few were calculated. The results show that the major constituents of the alloy include β-Mg17Al12 and Mg2Si phase , and no difference in the type of constituents between without ultrasonic vibration and with ultrasonic vibration. Without any ultrasonic vibration, the grain size and Mg2Si phase in AS41 alloy are co-structure with. However, the microstructure with fine uniform grains and Mg2Si particles are achieved with When the ultrasonic vibration intensity was too low or too high, coarse structures could be obtained. The analysis of refinement mechanism indicates that the acoustic cavitation and flows induced by ultrasonic vibration lead to the fine uniform microstructure.