【摘 要】
：
Hydration-heat-inhibiting materials(HIM) with polysaccharide as core material was prepared using microcapsule sustained-releasing technology, through a centrifugal spray granulation process after melting together. The preparation process parameters of HIM
【机 构】
：
State Key Laboratory of Green Building Materials,China Building Materials Academy,Beijing 100024,Chi
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Hydration-heat-inhibiting materials(HIM) with polysaccharide as core material was prepared using microcapsule sustained-releasing technology, through a centrifugal spray granulation process after melting together. The preparation process parameters of HIM were selected by the semi-adiabatic temperature rise test of cement paste. TAM air microcalorimeter was used to investigate the regulation performance of HIM on the hydration of cement. The influence of HIM on the microstructure of cement was investigated by XRD, SEM, and TG-DSC.The results showed that the most suitable wall material for HIM was polyethylene wax, the optimum polyethylene wax/polysaccharide mass ratio was 1, and the most effective particle size was 0.16-0.30 mm. Polysaccharide coated by polyethylene wax released slowly, and the peak heat release rate of cement could be reduced by 55.2％ after continuous regulaion. The regulation period continued to 120 h. HIM mainly decreased the C3S reaction rate, which resulted in a 39.2％ peak value reduction of hydration heat release rate. However, HIM had little regulation on C3A. The hydration heat release process of cement-based materials can be designed by adjusting the dosage of HIM.
其他文献
The physical performance of recycled asphalt was used as the main evaluation index to study the optimal range of a self-made rejuvenator. Through the penetration, viscosity and gel permeation chromatography (GPC) tests, the diffusion degree of the rejuven
The electrical conductivity of graphene/cement composite before and after carbonation was tested by a four-electrode method. The General Effective Media equation was adopted to fit the experiment results. EIS (electrochemical impedance spectroscopy) was e
A polarizing microscope, X-ray diffraction (XRD), fourier transform infrared spectrometer (FTIR), scanning electron microscope and energy dispersive spectrometer (SEM-EDS), X-ray photoelectron spectroscopy (XPS), and micro computed tomography (Micro CT) w
Nano-pellet α-Al2O3 was prepared using aluminum nitrate as precursor and urea as fuel by a fast method of solution combustion synthesis. The formation of the nano material was dependent on the molar ratio of fuel/oxidant, calcination temperature, and fore
Aluminum sol, dry gel, and film were prepared by sol-gel and a dipping-withdrawing method. The effect of polyethylene glycol (PEG) on the behavior of aluminum sol, gel, and film was investigated by DLS, rotary viscometer, XRD, IR, EPMA, and light microsco
A quantitative pH measuring method has been used to measure the pH of pure and blended cement mortars. The blended cement mortars incorporating supplementary cementitious materials (SCMs) such as fly ash (FA), ground granulated ballast furnace slag (GGBFS
With the risk of disappearing for the rock paintings considering long-term exposure in Helan Mountain, the freeze-thaw(F-T) cycling experiments were carried out with 12-hour F-T cycling (0, 10, 20, 30, and 40 F-T cycles) under five kinds of confining pres
TiSi2 reinforced boron phenolic composites (TP) and Vitreous silica fabric reinforced TiSi2/boron phenolic composites (VTP) were prepared by compression molding, and their thermal, mechanical, ablation properties were studied. TG results show that thermal
In order to facilitate self-compacting concrete to be better used in tunnel linings that can resist fires, a SiO2 aerogel-cement mortar coating was prepared. Based on the HC curve, a self compacting concrete cube specimens coated and uncoated with SiO2 ae
To reveal and utilize the interaction between Tamm plasmon polaritons (TPPs) and two-dimensional materials are promising for exploiting next-generation optoelectronic devices. Herein, the coupling mechanism between metal TPPs and monolayer WS2 along with