【摘 要】
：
Nano-pellet α-Al2O3 was prepared using aluminum nitrate as precursor and urea as fuel by a fast method of solution combustion synthesis. The formation of the nano material was dependent on the molar ratio of fuel/oxidant, calcination temperature, and fore
【机 构】
：
College of Materials Science and Engineering, Qingdao University of Science and Technology, Qingdao
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
【发表日期】
：
2021年6期
其他文献
分析了助听器芯片中∑-△ADC的降采样滤波器、上采样滤波器的原理及实现技术.优化滤波器结构和滤波器系数,降低了芯片面积.采用可编程配置的滤波器系数,实现通带平坦度与过渡带带宽、采样率之间的动态切换.采用SMIC 130 nm 1P8M CMOS工艺进行了MPW流片验证.结果 表明,该滤波器可支持16 kHz、32 kHz采样率,满足不同采样率助听器DSP的需求.级联后滤波器的通带纹波为0.001 dB,阻带衰减达80 dB,群延时之和最大值为3.877 ms,满足助听器信号转换电路的要求.
Electroless Plating of Ni Nanoparticles on WC to Assist Its Pressureless Sintering of WC-Ni Cemented
Ni nanoparticles were coated uniformly on the surface of WC powder via a facile electroless plating method (abbreviated as WCN-EP), and then consolidated for mechanical and corrosion resistance performance characterization, in comparison with hand mixed W
Effects of Lay-up Types of Out-of-autoclave Prepregs on Preparation Quality of L-shape Composite Lam
Effects of layer quantities and stacking sequences on L-shape composite manufacturing qualities in using OOA(out-of-autoclave) prepregs were studied. The mechanisms of air evacuated in 5 kinds of lay-ups were revealed by image analysis of cut surfaces and
Al2O3 particles reinforced hypereutectic Al-Si composites were prepared by in situ Fe2O3/Al reaction system. The thermodynamic analysis and microstructure evolution were investigated by differential scanning calorimetry, optical microscope, scanning elect
A new strategy to fabricate oxygen-promoted Cu,N co-doped carbon (OP-CuN@C) composites is reported. The strategy consists of only two simple steps: chemical polymerization and high temperature carbonization. Electrochemical measurements were conducted to
Preparation of Heavyweight Ultra-high Performance Concrete Using Barite Sand and Titanium-rich Heavy
The heavyweight ultra-high performance concrete (HUHPC) was prepared with barite sand partially replaced by titanium-rich heavy slag sand (THS) at replacement proportion of 0％, 30％, 50％, 70％ and 100％ in this work. The results show that THS incorporation c
Effects of Shale and CaO Incorporation on Mechanical Properties and Autogenous Deformationof Early-a
The pre-soaked shale employed as an internal curing agent and CaO employed as expansion agent were incorporated into concrete to investigate their effects on the mechanical properties and autogenous deformation of early-age concrete. We have conducted the
The physical performance of recycled asphalt was used as the main evaluation index to study the optimal range of a self-made rejuvenator. Through the penetration, viscosity and gel permeation chromatography (GPC) tests, the diffusion degree of the rejuven
The electrical conductivity of graphene/cement composite before and after carbonation was tested by a four-electrode method. The General Effective Media equation was adopted to fit the experiment results. EIS (electrochemical impedance spectroscopy) was e
A polarizing microscope, X-ray diffraction (XRD), fourier transform infrared spectrometer (FTIR), scanning electron microscope and energy dispersive spectrometer (SEM-EDS), X-ray photoelectron spectroscopy (XPS), and micro computed tomography (Micro CT) w