An investigation of lanthanum oxide (La2O3)addition to tungsten heavy alloy (WHA) with a ternary composition of W-7Ni-3Fe was reported in this study.The mixed p
【机 构】
：
School of Mechanical Engineering,VIT,Vellore 632014,India;Materials Research Institute,University Pa
论文部分内容阅读
An investigation of lanthanum oxide (La2O3)addition to tungsten heavy alloy (WHA) with a ternary composition of W-7Ni-3Fe was reported in this study.The mixed powders were sintered using spark plasma sintering(SPS) technique.La2O3 was added in increments of 0.25 wt％,0.50 wt％,0.75 wt％ and 1.00 wt％ to WHA,respectively.The sintered samples were characterized for microstructural evolution and mechanical properties.The influences of La2O3 addition on density,grain size,hard-ness,ultimate tensile strength (UTS) and ductility on W-7Ni-3Fe system were discussed in this study.The highest relative sintered density of 87.95％ was obtained for 0.25 wt％ La2O3 addition to W-7Ni-3Fe.The lowest grain size of 7.89 μtm was observed for 1.00 wt％ La2O3 addition.Similarly,the highest hardness and UTS of HV 533 and 1110 MPa,respectively,were also obtained for the same composition.Scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS) of the samples revealed homogenous distribution of La2O3 in the alloy matrix.Fractography of the sintered alloy samples revealed W-W intergranular fracture.
其他文献
The metal-organic-decomposed lanthanum cerium oxide(LaCeO2)solution was spin-coated on p-type Si substrate to form thin films.The method of microwave-assisted annealing was adopted to modify the surface properties of the deposited thin films.Th
为了有效监测局部放电信号,利用FPGA的高速并行处理能力,设计一种基于FPGA的特高频局部放电监测硬件实现系统。文中介绍了系统的硬件设计及FPGA实现原理。系统使用提升小波变换对采集数据进行脉冲提取,然后对有效脉冲进行特征提取,最后将提取的特征参数送入PC端,使用DBSCAN将脉冲的特征提取结果进行聚类分离。实验结果表明,基于高速FPGA设计的局部放电监测硬件系统能将不同脉冲信号有效分离。
A novel phenomenon of spontaneous positive exchange bias(PEB)is reported in SrFeO3-x/SrCoO3-x epitaxial bilayer without undergoing any magnetic field treatment.When inserting a thick SrTiO3(STO)nonmagnetic spacer(about 6 nm)into the bilayer interface,this
The increase in zinc content in Al-Zn-Mg-Cu alloys provides an effective method to enhance the strength.Transmission electron microscopy(TEM)and tensile test were employed to analyze the microstructure and tensile properties,respectively,of Al-9.3 Zn-2.0
Rapid oxidation takes place both in the laboratory and in industrial conditions when alloy 925 is contaminated by oxide powder,and the oxidation rate is much higher than normal.Herein,the rapid oxidation behavior and mechanism of alloy 925 were investigat
The Ti51.44Zr16.26Cu30Sn2.3(at%)amorphous filler alloy in a ribbon form was prepared by melt spinning.The Ti-6 Al-4 V alloy was brazed in vacuum furnace by using the Ti51.44Zr16.26Cu30
Al2O3-ZrO2-TiO2 coatings were successfully prepared by plasma spraying Al2O3-ZrO2 composite powders with and without TiO2 addition.The effects of TiO2 on the ph
For the purpose of elevated temperature service and weight reduction in aerospace vehicle applications,a novel Ti-Zr-Fe-Cu-Ni-Co-Mo filler metal was employed to join TiAl to Ni-based superalloy(GH536).The effects of brazing temperature on interfacial micr
The magnesium alloy has a unique advantage in 3C fields due to its high specific strength and excellent electromagnetic shielding characteristic.However,it is d
Ta-W alloys have unique properties but their applications at high temperatures are restricted due to their poor oxidation resistances.The addition of Al and Ti