据日本“铁钢”№5(1985)报道:东洋钢板公司针对连铸材用作镀锡原板时其耐蚀性比沸腾钢差这一现实,研究了钢成份和夹杂物的影响。采用成份为 C0.0025—0.12%;P0.006—0.024%;S0.005—0.028%;Al～0.104%;Cu0.004—0.14%的连铸材和沸腾钢进行试验。将各种钢分别置于50℃1M柠檬酸和0.1M 硫酸中,按 H_2发生量测定原
According to Japan’s “Iron and Steel” № 5 (1985) reported: Toyo plate for the continuous casting of tin plate when its corrosion resistance than boiling steel worse than the reality of the steel composition and inclusions. Using the composition of C0.0025-0.12%; P.006-0.024%; S0.005-0.028%; Al ~ 0.104%; Cu0.004-0.14% of continuous casting and boiling steel were tested. The various steel were placed in 50 ℃ 1M citric acid and 0.1M sulfuric acid, according to the amount of H_2 determination of the original