【摘 要】
：
本文研究了两种晶粒度的GH 698合金在700℃疲劳蠕变交互作用下的断裂寿命和形变行为.结果表明:在疲劳蠕变应力交互作用下的断裂寿命可以分成F,FC和C三个区.在FC及C区,交变应
【机 构】
：
北京钢铁学院材料系高温合金教研室,北京钢铁学院,北京钢铁学院,抚顺钢厂,抚顺钢厂,
论文部分内容阅读
本文研究了两种晶粒度的GH 698合金在700℃疲劳蠕变交互作用下的断裂寿命和形变行为.结果表明:在疲劳蠕变应力交互作用下的断裂寿命可以分成F,FC和C三个区.在FC及C区,交变应力的存在明显地阻碍蠕变形变过程,提高了断裂寿命.细晶处理后使这种阻碍作用加强,断裂寿命提高幅度变大.在大应力的疲劳区进行细晶处理,反而使合金寿命降低.
In this paper, the fracture life and deformation behavior of GH 698 alloy with two grain sizes under the fatigue-creep interaction at 700 ℃ are studied.The results show that the fracture life under fatigue-creep stress interaction can be divided into F, FC and C 3 In the FC and C zones, the existence of alternating stresses significantly hinders the creep and deformation process and improves the fracture life.After the fine-grained treatment, this impeding effect is strengthened and the improvement of the fracture life is increased. In the case of large-stress fatigue District fine grain processing, but to reduce the life of the alloy.
其他文献
冷轧辊的材质为GCr15钢,由于工作环境恶劣,常因磨损、局部剥落和出现裂纹等缺陷而报废。修复冷轧辊最好的方法是采用堆焊工艺,但由于冷轧辊材质的可焊性很差,且对表面质量要
前言在近代航空、航天、原子能等尖端科学技术中的发动机制造方面,对结构件特别是一些精密连接件,要求利用钎焊来解决连接问题,而钎焊料的研制则是首先应解决的重要课题。因
水,是生命的主要组成部分,于人类须臾不可离。多少世纪以来,人类习惯把日常生活所需的淡水看作是取之不尽、用之不竭的资源。这其实是一种错觉。今天,人类以空前的速度发展
男人有时十分重视自己的隐私,好像把生活中的片段纳入神秘的X档案里,让想了解他们的女人们,无法一窥究竟。不过百密必有一疏,男人在临睡前那短短的时刻里,他们最自我的生活
研究了微量Nb对MnV基的非调质微合金钢的冶金力学特性的影响。铌的加入进一步细化晶粒,促进析出作用。铌不单本身析出,而且促进钒的析出。配合以钢的其他成分调整,如降碳、增
<正> 从去年12月份以来,油价已由年底的每桶27美元降为今年元月的18美元,4月份后跌至10—15美元,目前在10—15美元之间浮动。油价的暴跌对阿拉伯产油国带来了巨大的经济损失,
Kolene corp公司新开发一种称为QPQ(quench—polisch—quench)的工艺。该工艺是以盐浴氮化为基本工序,以淬火、抛光为辅助工序。经过QPQ处理零件不仅耐磨性和疲劳强度高,而
2010年的民族题材电影延续了上一年的发展趋势,数量增多,且不乏精品。但真正在商业院线上放映的仍旧不多,多数只在北京大学生电影节、上海国际电影节、“北京放映”、华语青
一、前言磁性法测量残余奥氏体量准确性的关键在于标准试样的选择。关于标样的选择已进行多年的讨论。在理想的情况下,标样中应全部为铁磁相,并与试样中铁磁相有相同的化学
位于苏鲁豫皖四省接壤地域的淮海地区,包括十四个地市,总面积为14.9万平方公里,人口八千多万。该区南临长江三角洲,北近京津唐——毗邻我国两个最发达的经济区,并且西连我国