Nanocrystalline rare earth mixed oxides DyFe x Co 1- x O 3- δ were prepared by sol gel method and characterized by X ray diffraction (XRD), thermogravimetric analysis (TG DTA) and scanning electron microscope (SEM). The results show that DyFe x Co 1- x O 3- δ has the structure of perovskite type at 800 ℃ for 2 h calcination. The conductivity of the materials at different temperature was measured by four probe instrumentation and two pole method. The results show that the conductivity of mixed oxides DyFe x Co 1- x O 3- δ is higher than those of un mixed oxides DyFeO 3 and DyCoO 3 and the conductivity is the best at x =0.8 in the matter of DyFe x Co 1- x O 3- δ . The conductivity of these materials always increases with the temperature rising and there is an apparent change between 600 and 800 ℃. However, the spinodals are different with different ration of Fe 3+ and Co 3+ . This kind of oxide is a conductive pottery material.
Nanocrystalline rare earth mixed oxides DyFe x Co 1- x O 3- δ were prepared by sol gel method and characterized by X-ray diffraction (XRD), thermogravimetric analysis (TG DTA) and scanning electron microscope (SEM). The results show that DyFe x Co 1- x O 3- δ has the structure of perovskite type at 800 ° C for 2 h calcination. The conductivity of the materials at different temperature was measured by four probe instrumentation and two pole method. The results show that the conductivity of mixed oxides DyFe x Co 1- x O 3- δ is higher than those of unmixed oxides DyFeO 3 and DyCoO 3 and the conductivity is the best at x = 0.8 in the matter of DyFe x Co 1- x O 3- δ. The conductivity of these materials always increases with the temperature rising and there is an apparent change between 600 and 800 ° C. However, the spinodals are different with different ration of Fe 3+ and Co 3+. This kind of kind of oxide is a conductive pottery material.