摘自中国矿业大学北京研究生部研究生陈华辉的博士学位论文,导师:邵荷生 本文对16Mn钢、27SiMn钢、1Crl8Ni9不锈钢、氧一乙炔火焰热喷涂Al_2O_3复合陶瓷涂层和复合尼龙涂层进行了腐蚀一磨料磨损及腐蚀一冲蚀磨损试验。研究了pH值、载荷、冲击速度等因素对上述材料的腐蚀一磨损影响规律。探讨了钢、复合陶瓷涂层及复合尼龙涂层的腐蚀一磨损机制。建立了钢、复合陶瓷涂层和复合尼龙涂层的pH-v,(冲击速度)—V_E(腐蚀冲蚀率)立体图。推导出钢的腐蚀磨料磨损
From China University of Mining and Technology Beijing Graduate Department of Chen Huaihui doctoral dissertation, this article 16Mn steel, 27SiMn steel, 1Crl8Ni9 stainless steel, oxy-acetylene flame thermal spray Al 2 O 3 composite ceramic coating and composite nylon coating corrosion-abrasive wear And corrosion of an erosion wear test. The influence of pH, load, impact velocity and other factors on corrosion-wear of the above materials was studied. The corrosion-wear mechanism of steel, composite ceramic coating and composite nylon coating was discussed. A pH-v (impact velocity) -V_E (erosion erosion rate) perspective view of steel, composite ceramic coating and composite nylon coating was established. The corrosive abrasion of steel was deduced