Reaction synthesis process has been used to develop γ titanium aluminide using elemental powders. Powder mixture of Ti-48 at. pct Al was prepared in ball mill and reaction synthesis was carried out in hot press with varying temperature and pressure. Titanium aluminide synthesized under high pressure and temperature resulted in better properties with respect to densification, homogenization response, mechanical properties and oxidation resistance as compared to that synthesized under low pressure and temperature. Al rich phases were observed in as-synthesized condition in all the experiments. However, some Ti rich phases were also found in high pressure-temperature synthesized samples. Density, hardness and tensile strength have been correlated with applied pressure through empirical relations. Variation in density with pressure is found to be logarithmic whereas hardness and tensile strength variation with pressure is polynomial.
Reaction synthesis process has been used to develop γ titanium aluminide using elemental powders. Powder mixture of Ti-48 at. Pct Al was prepared in ball mill and reaction synthesis was carried out in hot press with varying temperature and pressure. pressure and temperature resulted in better properties with respect to densification, homogenization response, mechanical properties and oxidation resistance as compared to that synthesized under low pressure and temperature. However, some Ti richness were also found in high pressure-temperature synthesized samples. Density, hardness and tensile strength have been correlated with applied pressure through empirical relations. Variation in density with pressure is found to be logarithmicstanding hardness and tensile strength variation with pressure is polynomial.