韩国Pohan科技大学Se Min Park等人研究了脱碳工艺参数对Fe-3%Si-0.3%C钢板织构和磁性影响,得出如下结论:(1)在真空度1.3×10~(-3)Pa条件下,经过1 323K保温10min。再以20K/s速度冷却到室温,此时钢中发生了α→γ→α相转变,表面层形成明显的<100>//ND织构;(2)以85%压下率冷轧到0.35mm时,织构由强的α纤维(<110>//RD)、弱的γ纤维(<111>//ND)及{001}<110>组成;(3)1.3×10~(-3) Pa
Se Min Park and others from Pohan University of Science and Technology of Korea studied the effect of decarburization process parameters on the texture and magnetic properties of Fe-3% Si-0.3% C steel. The conclusions are as follows: (1) In the vacuum degree of 1.3 × 10 -3 ) Pa conditions, after 1 323K insulation 10min. And then cooled to room temperature at a rate of 20K / s. At this time, α → γ → α phase transformation occurred in the steel, and the surface layer formed obvious <100> // ND texture. (2) The texture is composed of strong α fiber (<110> // RD), weak γ fiber (<111> // ND) and {001} <110> 3) Pa