Magnetic properties and structure of (001)-oriented [CoPt/C]n/Ag nanocomposite films on the glass su

• 作 者: JIN Tao XU Xiaohong WANG Fang LI Xiaoli JIANG Fengxian YANG Zhiguang
• 机 构: School of Chemistry and Materials Science, Shanxi Normal University, Linfen 041004, China
• 出 处: 稀有金属（英文版）
• 发表日期: 2006年3期
• 关键词: [CoPt/C]n/Ag multilayer films (001) orientation C content number of repetition

The highly (001) oriented triple system of [CoPt/C]n/Ag films was deposited on glass substrates by DC and RF magnetron sputtering. After annealing at 600℃ for 30 min, thin films become magnetically hard with coercivities in the range of 160-875 kA/m because of high anisotropy associated with the L10 ordered phase. C doping plays an important role in improving (001) texture and reducing the intergrain interactions. The oriented growth of CoPt films was influenced strongly by the number of repetitions (n) of CoPt/C. By controlling the C content and the number of repetitions (n) of CoPt/C, nearly perfect (001) orientation can be obtained in the [CoPt3 nm/C3 nm]5/Ag50 nm.