Poly(styrene-glycidyl methacrylate) particles having bowl-shaped hollow structures were synthesized by swollen seed emulsion polymerization. The PS emulsion synthesized through soap-free emulsion polymerization was swollen by toluene, and then the mixture of second monomers was added under polymerization condition. So a thin shell of poly(styrene-glycidyl methacrylate) cross-linked by triethylene glycol diacrylate was formed around the swollen PS particle. The bowl-shaped particles were obtained after the collapsing of the thin shell when the toluene emanated from the particles, but the shapes were effected by the degrees of cross-linking. The shape of the particles was observed by SEM. The release behavior of solvent from the particles was examined by TG.
Poly (styrene-glycidyl methacrylate) particles having bowl-shaped hollow structures were synthesized by swollen seed emulsion polymerization. The PS emulsion synthesized through soap-free emulsion polymerization was swollen by toluene, and then the mixture of second monomers was added under polymerization conditions. So a thin shell of poly (styrene-glycidyl methacrylate) cross-linked by triethylene glycol diacrylate was formed around the swollen PS particle. The bowl-shaped particles were obtained after the collapsing of the thin shell when the toluene emanated from the particles, but the shapes were effected by the degrees of cross-linking. The shape of the particles was observed by SEM. The release behavior of solvent from the particles was examined by TG.