The sintering technology for mixed powdered extrusion rods of different proportions of stainless steel to magnesiapartially stabilized zirconia (PSZ) was investigated. The effects of some sintering parameters including holdingtime, atmosphere and protective gas pressure on shrinkage, relative density, microstructure, micro-Vickers hardnessand compression strength of sintered samples were mainly researched. The experimental results are as follows: (1)The shrinkage and the relative density of the sintered samples decrease as increasing stainless steel content in thecomposite, except for the case containing 90 percent of stainless steel; (2) The porosity in PSZ matrix rises asincreasing the stainless steel content in the composite; (3) Longer sintering holding time, higher sintering vacuumand gas-pressure sintering process not only enhance the relative density, but also improve microstructure of composite;(4) Micro-Vickers hardness of PSZ matrix decreases as increasing stainless steel content, while that of stainless steelparticles in sintered samples varies unnoticeably.