Materials such as Koch AH-70,basalt aggregate,limestone powder and graphite particles were used to prepare conductive asphalt concrete,which is a new type of multifunctional concrete.The mix proportion by weight was shown as follows.Fine aggregates (2.36-4.75 mm)∶fine aggregates (<2.36mm)∶limestone powder∶asphalt=120∶240∶14∶30.The content of added graphite particles ranged from 0% to 20%(by the weight of asphalt concrete).A conductive asphalt concrete with a resistivity around 10-10 3Ω·m was obtained.Special attention was paid to the effects of graphite content,graphite physical-chemical properties,asphalt content and temperature on the resistivity.Furthermore,an attempt was made to develop an electrically conductive model for asphalt concrete.
Materials such as Koch AH-70, basalt aggregate, limestone powder and graphite particles were used to prepare conductive asphalt concrete, which is a new type of multifunctional concrete. The mix proportion by weight was shown as follows. Fine aggregates (2.36-4.75 mm ): Aggregates (<2.36mm): limestone powder: asphalt = 120: 240: 14: 30. The content of added graphite particles ranged from 0% to 20% a resistivity around 10-10 3 Ω · m was obtained. Special attention was paid to the effects of graphite content, graphite physical-chemical properties, asphalt content and temperature on the resistivity. Furthermore, an attempt was made to develop an electrically conductive model for asphalt concrete.