Hollow spheres of hexagonal ferrite BaCo2Fe16O27 were fabricated through a spray pyrolysis technique using co-precipitation ferrite powder precursor as material
【机 构】
：
Energy Source and Environmental Engineering Department,State Key Laboratory of Advanced Technology f
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Hollow spheres of hexagonal ferrite BaCo2Fe16O27 were fabricated through a spray pyrolysis technique using co-precipitation ferrite powder precursor as materials, followed by calcinations in an air atmosphere. The phase composition, micro-morphology, and static magnetic property of the particles were measured by XRD, SEM, and VSM. The results indicate that the method for preparation of ferrite hollow microspheres (FHM) results in a broad particles size distribution. The density of FHM decreased from 5.31 g/cm3 to 2.31 g/cm3. When the heating rate was 5 ℃/min, and temperature was 1 200 ℃ for 4 hours, pure W-type ferrites were formed. With the heat treatment temperature and time increasing, the crystal structure becomes perfect, the saturation magnetization is increased and the coercive force is decreased.
其他文献
The effects of different substrates on the structure and hydrogen evolution from a-Si:H thin films deposited by plasma enhanced chemical vapour deposition were
A series of nanocomposite thin films, composed of Nd2Fe14B and α-Fe, has been prepared by DC-magnetron sputtering combined ion beam sputtering onto Si (100) su
By using the spark plasma sintering process, Ti2AlC/TiAl composite with the addition of Niobium (Nb) was prepared in-situ and the microstructure of Ti2AlC/TiAl
Isothermal and cyclic oxidation behaviors of chromium samples with and without nanometric CeO2 coating were studied at 900 ℃ in air. Scanning electron microsco
CdGd2(WO4)4-δ single crystal was grown using the Czochralskis method. The crystal structure was tetragonal scheelite with lattice parameters a=b=0.5203 nm and
Ceramic microspheres were prepared by using Chinese bauxite as raw materials through the centrifugal spray drying method. The control technology of microsphere
Ni-W-P-CeO2-SiO2 nano-composite coatings were prepared on the carbon steel surface by pulse co-deposition of nickel, tungsten, phosphorus, nano-CeO2 and nano-Si
Investigation into the magnets with different squareness of hysteresis loop (SHL) reveals that the microstructure of sintered NdFeB magnets has great effects on
A novel method was applied to the surface modification of the metal hydride(MH) electrode of MH/Ni batteries. Both sides of the electrode were plated with a thi
Conducting blends of polyacrylonitrile (PAN) copolymer and dodecylbenzene sulfonic acid doped polyaniline (PANI-DBSA) were prepared by solution blending of the