The effect of Ce,La and mischmetal on the solidification structure of Fe-36Ni invar alloy was investigated.The results show that great amounts of high-melting point compounds (Ce2O3,La2O2S and (Ce,La)2O2S) respectively formed in the alloy with the addition of Ce,La or mischmetal.Based on the theory of lattice misfit,the lattice misfit between the (0001) surfaces of Ce2O3,Ce2O2S and La2O2S and (100) surface of Fe-36Ni invar alloy were 6.21%,5.77% and 5.42%,respectively,which are relatively low.Therefore,Ce2O3 ,La2O2S and (Ce,La)2O2S could serve as the core of heterogeneous nucleation,improve the equiaxed grain ratio,reduce the equiaxed grain size and refine the solidification structure of alloy.
The effect of Ce, La and mischmetal on the solidification structure of Fe-36Ni invar alloy was investigated. The results show that great amounts of high-melting point compounds (Ce2O3, La2O2S and (Ce, La) 2O2S) respectively formed in the alloy with the addition of Ce, La or mischmetal. Based on the theory of lattice misfit, the lattice misfit between the (0001) surfaces of Ce2O3, Ce2O2S and La2O2S and (100) surface of Fe-36Ni invar alloy were 6.21%, 5.77% and 5.42%, respectively, which are relatively low.Therefore, Ce2O3, La2O2S and (Ce, La) 2O2S could serve as the core of heterogeneous nucleation, improve the equiaxed grain ratio, reduce the equiaxed grain size and refine the solidification structure of alloy .