With Gleeble-1500 system,the influences of rolling temperature,finishing temperature and cooling rate on the mechanical properties of two ultra-high strength steels were analyzed.The microstructure of the hot rolled specimens was observed by optical microscope,TEM and SEM.The TRIP of HSLA steels was studied.The results show that the yield stress of 700 MPa can be reached for two steels.The controlled rolling and controlled cooling technology has different effects on two steels,but it is rational to adopt finishing temperature 800℃for both of them.The microstructure of the steels is mainly bainite,and the influence factors of mechanical properties are the size of bainite,and the size,distribution,composition and morphology of secondary phases.The deformation of high molybdenum steels at a high temperature with a high cooling rate would promote TRIP.
With Gleeble-1500 system, the influences of rolling temperature, finishing temperature and cooling rate on the mechanical properties of two ultra-high strength steels were analyzed. The microstructure of the hot rolled specimens was observed by optical microscope, TEM and SEM. The TRIP of HSLA steels was studied. The results show that the yield stress of 700 MPa can be reached for two steels. The controlled rolling and controlled cooling technology has different effects on two steels, but it is rational to adopt finishing temperature 800 ℃ for both of the microstructure of the steels is mainly bainite, and the influence factors of mechanical size are the size of bainite, and the size, distribution, composition and morphology of the secondary phases. deformation of high molybdenum steels at a high temperature with a high cooling rate would promote TRIP.