铝及铝合金常温阳极化是南昌航空工业学院与我厂共同试验的一项新工艺。试验工作结束后,于一九七八年十二月投入试生产,在试生产中配制了3600升电解液。通过几年的试生产,已基本掌握了这项新工艺,目前已配30000升槽子用于所有零件生产。从试生产中表明,该工艺在40～45℃下也能获得满意的阳极化膜层,这是本工艺的最大优点,也使阳极化工艺取消制冷设备成为可能。在试生产中,得到南昌航空工业学院的技
At room temperature anodized aluminum and aluminum alloy Nanchang Institute of Aeronautical Industry and our joint test of a new technology. After the trial work was completed, it was put into trial production in December 1978 and 3600 liters of electrolyte were prepared in pilot production. After several years of pilot production, this new process has been basically mastered. Currently, 30,000 liter tanks have been used for the production of all parts. From the trial production showed that the process at 40 ~ 45 ℃ can also be satisfied with the anodized film, which is the biggest advantage of this process, but also to enable the anodizing process to cancel the refrigeration equipment possible. In trial production, Nanchang Institute of Aviation Technology